PPS DURAFIDE® 6165A4-HF2000 JAPAN POLYPLASTIC
140
Unit Price:$2876 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 100MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant wear resistant
- Application Areas:Fiber grade
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | TD | ASTMD955 | 0.30to0.50 | % |
| TD | ISO294-4 | 0.30to0.70 | % | |
| MD | ISO294-4 | 0.20to0.60 | % | |
| ISO 2577 | 0.2-0.6 | % | ||
| MD | ASTMD955 | 0.10to0.20 | % | |
| 吸水率 | 23℃ | ISO 62 | 0.02 | % |
| 饱和,23°C | ISO62 | 0.020 | % | |
| SpecificHeatCapacityofMelt | 内部方法 | 1600 | J/kg/°C | |
| 特定体积 | ASTMD792 | 0.502 | cm³/g | |
| SpiralFlow | 内部方法 | 15.5 | ||
| 熔体质量流动速率 | ASTMD1238 | 7.5 | g/10min | |
| 密度 | ISO1183 | 1.95 | g/cm³ | |
| ASTMD792 | 2.00 | g/cm³ | ||
| ISO 1183 | 1.95 | g/cm³ |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 悬臂梁无缺口冲击强度 | 23°C | ISO180/1U | 20 | kJ/m² |
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| 23°C | ISO179/1eA | 7.0 | kJ/m² | |
| 悬壁梁缺口冲击强度 | -30°C | ISO180/1A | 6.0 | kJ/m² |
| 23°C | ISO180/1A | 6.0 | kJ/m² | |
| 悬臂梁缺口冲击强度 | 23℃ | ISO 180/1A | 6 | kJ/m² |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 20 | kJ/m² |
| 23°C | ISO179/1eU | 20 | kJ/m² | |
| 拉伸模量 | ISO 527-1 | 19000 | Mpa | |
| ISO527-2/1A/1 | 19000 | Mpa | ||
| 拉伸强度 | 断裂,23°C | ASTMD638 | 131 | Mpa |
| 断裂 | ISO527-2/1A/5 | 130 | Mpa | |
| ISO 527-1 | 130 | Mpa | ||
| 伸长率 | 断裂 | ISO 527-1 | 1.2 | % |
| 断裂,23°C | ASTMD638 | 1.3 | % | |
| 断裂 | ISO527-2/1A/5 | 1.2 | % | |
| 洛氏硬度 | ISO 294-4 | 100 | M-scale | |
| M级 | ASTMD785 | 100 | ||
| M级 | ISO2039-2 | 100 | ||
| 弯曲模量 | ISO 178 | 18800 | Mpa | |
| 23°C | ISO178 | 18800 | Mpa | |
| 弯曲强度 | ISO178 | 210 | Mpa | |
| ISO 178 | 210 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 玻璃转化温度 | ISO11357-2 | 90.0 | °C | |
| 热变形温度 | 0.45MPa,退火 | ASTMD648 | 280 | °C |
| 1.8MPa,未退火 | ASTMD648 | 266 | °C | |
| 1.8MPa,未退火 | ISO75-2/A | 270 | °C | |
| 8.0MPa,未退火 | ISO75-2/C | 215 | °C | |
| 1.80Mpa | ISO 75-1 | 270 | °C | |
| 阻燃等级 | 0.750mm | UL94 | V-0 | |
| 线性热膨胀系数 | MD | ISO11359-2 | 1.9E-05 | cm/cm/°C |
| TD | ISO11359-2 | 2.4E-05 | cm/cm/°C | |
| 熔融温度 | ISO11357-3 | 280 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 介电强度 | IEC60243-1 | 25 | KV/mm | |
| 相对电容率 | 1MHz | IEC60250 | 5.60 | |
| 漏电起痕指数 | IEC60112 | 175 | V | |
| 耗散因数 | 1kHz | ASTMD150 | 1E-03 | |
| 1MHz | ASTMD150 | 9E-04 | ||
| 1MHz | IEC60250 | 2E-03 | ||
| 表面电阻率 | IEC60093 | >1.0E+15 | ohms | |
| 介电常数 | 1kHz | ASTMD150 | 5.40 | |
| 1MHz | ASTMD150 | 5.60 | ||
| 耐电弧性 | ASTMD495 | 182 | sec | |
| 体积电阻率 | ASTMD257 | 1E+16 | ohms·cm | |
| IEC60093 | >1.0E+17 | ohms·cm |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL阻燃等级 | 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 | ||
| 3.0mm | UL94 | 5VA | ||
| 极限氧指数 | ISO4589-2 | 53 | % |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| SpecimenThickness-Shrinkage | 内部方法 | 3.18 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.