PPS Torelina® A610MG1 TORAY JAPAN
150
Unit Price:$5725 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 87MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low liquidity
- Application Areas:Automotive Applications sporting goods
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.60 | % |
| MD:3.00mm4 | 内部方法 | 0.20 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.020 | % |
| density | ASTM D792/ISO 1183 | 1.96 | ||
| Shrinkage rate | ASTM D955 | 0.2 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.02 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 1 | % | |
| tensile strength | ASTM D638/ISO 527 | 95 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 123 | ||
| Bending modulus | ASTM D790/ISO 178 | 20 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 245 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | Yield,23°C | ISO527-2 | 155 | Mpa |
| elongation | Break,23°C | ISO527-2 | 1.0 | % |
| Bending modulus | 23°C | ISO178 | 20000 | Mpa |
| bending strength | 23°C | ISO178 | 245 | Mpa |
| shear strength | 23°C | JISK7214 | 60.0 | Mpa |
| Friction coefficient | 0.30 | |||
| Taber abraser | 1000Cycles | ISO9352 | 70.0 | mg |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 22 | kJ/m² |
| Rockwell hardness | R-Scale | ISO2039-2 | 123 | |
| Charpy impact strength | ASTM D256/ISO 179 | 9 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 22 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | V-0 | ||
| Hot deformation temperature | ASTM D648/ISO 75 | >260 | ℃（℉） | |
| melting point | 278 | ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.8 | mm/mm.℃ | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 260 | °C |
| Melting temperature | ISO11357-3 | 278 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.8E-05 | cm/cm/°C |
| TD | ISO11359-2 | 2.7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 1E+16 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 22 | KV/mm | |
| Dielectric constant | 23°C,1MHz | IEC60250 | 4.90 | |
| Dissipation factor | 23°C,1MHz | IEC60250 | 2E-03 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.73mm | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 110 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.