PPS Torelina® A305M TORAY JAPAN
153
Unit Price:$4925 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 55.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan high strength Flame retardant Filler: Glass mineral 50% filler by weight
- Application Areas:Electrical appliances Sports Equipment Automotive sector Electronic field Electrical field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.85 | ||
| Shrinkage rate | ASTM D955 | 0.16 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.02 | % | |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.75 | % |
| MD:3.00mm4 | 内部方法 | 0.16 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.020 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | Yield,23°C | ISO527-2 | 180 | Mpa |
| elongation | Break,23°C | ISO527-2 | 1.3 | % |
| Bending modulus | 23°C | ISO178 | 17000 | Mpa |
| bending strength | 23°C | ISO178 | 260 | Mpa |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 40 | kJ/m² |
| Rockwell hardness | R-Scale | ISO2039-2 | 122 | |
| elongation at break | ASTM D638/ISO 527 | 0.9 | % | |
| tensile strength | ASTM D638/ISO 527 | 140 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 122 | ||
| Bending modulus | ASTM D790/ISO 178 | 190 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 220 | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 8 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 740 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | V-0 | ||
| Hot deformation temperature | ASTM D648/ISO 75 | >260 | ℃（℉） | |
| melting point | 278 | ℃（℉） | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 260 | °C |
| Melting temperature | ISO11357-3 | 278 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.8E-05 | cm/cm/°C |
| TD | ISO11359-2 | 3E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 1E+16 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 24 | KV/mm | |
| Dielectric constant | ASTM D150/IEC 60250 | 5 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 1014 | Ω.cm | |
| DielectricConstant | 23°C,1MHz | IEC60250 | 5.00 | |
| Dissipation factor | 23°C,1MHz | IEC60250 | 2E-03 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.35mm | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 120 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.