PPS DURAFIDE® 1130A1 JAPAN POLYPLASTIC
210
Unit Price:$3613 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 110MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength High temperature resistan High toughness Flame retardant enhance
- Application Areas:Household appliances Household appliances Fitness equipment Automotive sector Bottle cap
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO62 | 0.030 | % |
| density | ISO 1183 | 1.57 | g/cm³ | |
| Melt viscosity | 310℃,1000/sec | ISO 11443 | 350 | Pa·s |
| Water absorption rate | 23℃,水中24hr | ISO 62 | 0.01 | % |
| Shrinkage rate | Flow ，80℃×2mmt | 0.3 | % | |
| Across Flow ，80℃×2mmt | 0.6 | % | ||
| density | ASTM D792/ISO 1183 | 1.57 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.01 | % | |
| Melt viscosity | 310°C,1000sec^-1 | ISO11443 | 350000 | mPa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| bending strength | ISO 178 | 245 | Mpa | |
| Bending modulus | ISO 178 | 10000 | Mpa | |
| Impact strength of simply supported notched beam | ISO 179/1eA | 10.0 | kJ/m² | |
| tensile strength | ISO 527-1,2 | 170 | Mpa | |
| Fracture strain | ISO 527-1,2 | 2 | % | |
| tensile strength | ASTM D638/ISO 527 | 170 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 10000 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 245 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ISO527-2 | 170 | Mpa | |
| elongation | Break | ISO527-2 | 2.0 | % |
| Bending modulus | ISO178 | 10000 | Mpa | |
| bending strength | ISO178 | 245 | Mpa | |
| Rockwell hardness | M-Scale | ISO2039-2 | 105 | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 2 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | V-0 | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 260 | °C |
| Linear coefficient of thermal expansion | MD | 内部方法 | 2E-05 | cm/cm/°C |
| TD | 内部方法 | 4E-05 | cm/cm/°C | |
| Load deformation temperature | 1.8MPa | ISO 75-1 | 260 | °C |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 2 | ×10-5/℃ |
| Across Flow | 4 | ×10-5/℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257/IEC 60093 | 3.0 x 10^16 | Ω.cm | |
| IEC60093 | 3E+16 | ohms·cm | ||
| Dielectric strength | 3.00mm | IEC60243-1 | 16 | KV/mm |
| Relative permittivity | 1kHz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 4.00 | ||
| Dissipation factor | 1kHz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 2E-03 | ||
| 耐电弧性 | IEC60250 | 124 | sec | |
| Leakage Trace Index | IEC60112 | 150 | V | |
| Volume resistivity | IEC 60093 | 3×1016 | Ω·cm | |
| Dielectric loss factor | 3mmt | IEC 60243-1 | 16 | KV/mm |
| Surface resistivity | IEC 60093 | 2×1017 | Ω | |
| Resistant to conductive tracks | IEC 60112 | 150 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ColourNumber | HF2000/HD9050 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.