LCP VECTRA® A130D1-CB3002 CELANESE USA
159
Unit Price:$6194 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced Thermal stability Chemical resistance
- Application Areas:Electrical field Electronic field Household appliances Household appliances
- Color:--
- Grade:--
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 横向流量 | ISO 294-4 | 0.40 | % |
| 流量 | ISO 294-4 | 0.20 | % | |
| 吸水率 | 平衡, 23°C, 50% RH | ISO 62 | 0.040 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸蠕变模量 | 1 hr | ISO 899-1 | 12600 | Mpa |
| 1000 hr | ISO 899-1 | 10900 | Mpa | |
| 拉伸模量 | ISO 527-2/1A | 15000 | Mpa | |
| 拉伸强度 | 断裂 | ISO 527-2/1A/5 | 190 | Mpa |
| 伸长率 | 断裂 | ISO 527-2/1A/5 | 2.1 | % |
| 洛氏硬度 | M 计秤 | ISO 2039-2 | 85 | |
| 弯曲模量 | 23°C | ISO 178 | 14500 | Mpa |
| 弯曲强度 | 23°C | ISO 178 | 280 | Mpa |
| 悬臂梁无缺口冲击强度 | 23°C | ISO 180/1U | 29 | kJ/m² |
| 压缩应力 | 1% 应变 | ISO 604 | 100 | Mpa |
| 压缩模量 | ISO 604 | 14500 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火 | ISO 75-2/B | 250 | °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 235 | °C | |
| 8.0 MPa, 未退火 | ISO 75-2/C | 190 | °C | |
| 维卡软化点 | ISO 306/B50 | 160 | °C | |
| 熔融温度 | ISO 11357-3 | 280 | °C | |
| 线性热膨胀系数 | 流动 | ISO 11359-2 | 6.0E-6 | cm/cm/°C |
| 横向 | ISO 11359-2 | 2.3E-5 | cm/cm/°C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 介电强度 | IEC 60243-1 | 31 | KV/mm | |
| 耗散因数 | 100 Hz | IEC 60250 | 0.016 | |
| 1 MHz | IEC 60250 | 0.018 | ||
| 表面电阻率 | IEC 60093 | > 1.0E+15 | ohms | |
| 耐电弧性 | 内部方法 | 140 | sec | |
| 体积电阻率 | IEC 60093 | 1.0E+15 | ohms·cm | |
| 相对电容率 | 100 Hz | IEC 60250 | 4.20 | |
| 1 MHz | IEC 60250 | 3.70 | ||
| 漏电起痕指数 | IEC 60112 | 175 | V |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 150 | °C | ||
| 建议的最大水分含量 | 0.010 | % | ||
| 加工（熔体）温度 | 285 到 295 | °C | ||
| 模具温度 | 80 到 120 | °C | ||
| 干燥时间 | 4.0 到 6.0 | hr | ||
| 料筒后部温度 | 270 到 280 | °C | ||
| 料筒中部温度 | 275 到 285 | °C | ||
| 料筒前部温度 | 280 到 290 | °C | ||
| 射嘴温度 | 290 到 300 | °C | ||
| 背压 | < 3.00 | Mpa | ||
| 料斗温度 | 20 到 30 | °C | ||
| 注射速度 | 快速 |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 极限氧指数 | ISO 4589-2 | 45 | % | |
| UL 阻燃等级 | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.