LCP VECTRA® B230 BK CELANESE USA
134
Unit Price:$6194 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Conductive High rigidity high strength Halogen-free Flame retardant Carbon fiber reinforced
- Application Areas:Metal substitution
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 横向流量 | ISO 294-4 | 0.10 | % |
| 流量 | ISO 294-4 | 0.0 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 悬臂梁无缺口冲击强度 | 23°C | ISO 180/1U | 12 | kJ/m² |
| 简支梁无缺口冲击强度 | 23°C | ISO 179/1eU | 15 | kJ/m² |
| 压缩应力 | 1% 应变 | ISO 604 | 204 | Mpa |
| 拉伸模量 | ISO 527-2/1A | 31800 | Mpa | |
| 拉伸强度 | 断裂 | ISO 527-2/1A/5 | 200 | Mpa |
| 伸长率 | 断裂 | ISO 527-2/1A/5 | 0.70 | % |
| 洛氏硬度 | M 计秤 | ISO 2039-2 | 99 | |
| 弯曲模量 | 23°C | ISO 178 | 25500 | Mpa |
| 弯曲强度 | 23°C | ISO 178 | 300 | Mpa |
| 压缩模量 | ISO 604 | 33000 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 线性热膨胀系数 | 流动 | ISO 11359-2 | 1.0E-6 | cm/cm/°C |
| 横向 | ISO 11359-2 | 9.0E-6 | cm/cm/°C | |
| 维卡软化点 | ISO 306/B50 | 167 | °C | |
| 热变形温度 | 0.45 MPa, 未退火 | ISO 75-2/B | 250 | °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 235 | °C | |
| 8.0 MPa, 未退火 | ISO 75-2/C | 186 | °C | |
| 熔融温度 | ISO 11357-3 | 280 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 相对电容率 | 1 MHz | IEC 60250 | 32.0 | |
| 表面电阻率 | IEC 60093 | 1.0E+2 | ohms | |
| 体积电阻率 | IEC 60093 | 1.0E+5 | ohms·cm |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 150 | °C | ||
| 建议的最大水分含量 | 0.010 | % | ||
| 加工（熔体）温度 | 285 到 300 | °C | ||
| 模具温度 | 80 到 120 | °C | ||
| 干燥时间 | 6.0 到 8.0 | hr | ||
| 料筒后部温度 | 270 到 280 | °C | ||
| 料筒中部温度 | 275 到 285 | °C | ||
| 料筒前部温度 | 280 到 290 | °C | ||
| 射嘴温度 | 290 到 300 | °C | ||
| 背压 | < 3.00 | Mpa | ||
| 料斗温度 | 20 到 30 | °C | ||
| 注射速度 | 快速 |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.