LCP VECTRA® A515D-2 BK CELANESE GERMANY
153
Unit Price:$6193 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Good liquidity Hydrolysis resistance Halogen-free Flame retardant Mineral reinforcement
- Application Areas:Fitness equipment Automotive Applications Thin walled products
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 0.60 | % |
| 流量 | ISO 294-4 | 0.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M -Sale | ISO 2039-2 | 63 | |
| Tensile modulus | ISO 527-2/1A | 10500 | Mpa | |
| tensile strength | Break | ISO 527-2/1A/5 | 175 | Mpa |
| elongation | Break | ISO 527-2/1A/5 | 4.5 | % |
| Bending modulus | 23°C | ISO 178 | 11000 | Mpa |
| bending strength | 23°C | ISO 178 | 175 | Mpa |
| Compressive modulus | ISO 604 | 9500 | Mpa | |
| Compressive stress | 1% Strain | ISO 604 | 61.0 | Mpa |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 | kJ/m² |
| Cantilever beam without notch impact strength | 23°C | ISO 180/1U | 130 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 232 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 185 | °C | |
| 8.0 MPa, Unannealed | ISO 75-2/C | 103 | °C | |
| vicat softening point | ISO 306/A50, ISO 306/B50 | 149 | °C | |
| Melting temperature | ISO 11357-3 | 280 | °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 0.0 | cm/cm/°C |
| Across Flow | ISO 11359-2 | 3.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | 1.0E+15 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 40 | KV/mm | |
| Relative permittivity | 100 Hz | IEC 60250 | 3.80 | |
| 1 MHz | IEC 60250 | 3.20 | ||
| Dissipation factor | 100 Hz | IEC 60250 | 0.010 | |
| 1 MHz | IEC 60250 | 0.020 | ||
| Arc resistance | 内部方法 | 145 | sec | |
| Leakage Trace Index | IEC 60112 | 175 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 150 | °C | ||
| drying time | 4.0 到 6.0 | hr | ||
| Suggested maximum moisture content | 0.010 | % | ||
| Hopper temperature | 20 到 30 | °C | ||
| Temperature at the rear of the barrel | 270 到 280 | °C | ||
| Temperature in the middle of the barrel | 275 到 285 | °C | ||
| Temperature at the front of the material cylinder | 280 到 290 | °C | ||
| Spray nozzle temperature | 290 到 300 | °C | ||
| Processing (melt) temperature | 285 到 295 | °C | ||
| Mold temperature | 80 到 120 | °C | ||
| Injection speed | 快速 | |||
| Back pressure | < 3.00 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.