Thermal Properties	Test Condition	Test Method	Test Result
Melt Temperature			30-95 °C
RTI,Mechanical with Impact	3.0mm	UL 746-B	220 °C
	RTI,Mechanical with Impact	3.0mm	UL 746-B	240 °C
	RTI,Mechanical with Impact	RTI,Mechanical with Impact	1.0mm	UL 746-B	240 °C
Glass Transition Temperature		ASTM D-3418	120 °C
RTI,Electrical	3.0mm	UL 746-B	240 °C
RTI,Mechanical with Impact	1.0mm	UL 746-B	210 °C
Drying Temperature			135 °C
Melting Temperature		ASTM D-3418	335 °C
RTI,Electrical	1.0mm	UL 746-B	240 °C
Heat Deflection Temperature	1.80MPa	ASTM D-648	272 °C
Glass Transition Temperature			350-360 °C
Heat Deflection Temperature		ASTM D648/ISO 75	272 ℃（℉）
Melting Temperature			335 ℃（℉）

Mechanical Properties	Test Condition	Test Method	Test Result
Izod Impact Strength	3.2mm	ASTM D-256	85 J/m
Tensile Elongation?(Break)	3.2mm	ASTM D-638	1.4 %
Flexural Strength	3.2mm	ASTM D-790	177 Mpa
Tensile Strength	3.2mm	ASTM D-638	132 Mpa
Flexural Modulus	3.2mm	ASTM D-790	15200 Mpa
Izod notch impact strength		ASTM D256/ISO 179	85 kg·cm/cm(J/M)ft·lb/in
Tensile Elongation?(Break)		ASTM D638/ISO 527	1.4 %
Tensile Strength		ASTM D638/ISO 527	132 kg/cm²(MPa)[Lb/in²]
Flexural Modulus		ASTM D790/ISO 178	15200 kg/cm²(MPa)[Lb/in²]
Flexural Strength		ASTM D790/ISO 178	177 kg/cm²(MPa)[Lb/in²]

Other	Test Condition	Test Method	Test Result
Rating@Thickness		UL 746-B	V-0
Thickness Tested		UL 94	1.5 mm

Physical Properties	Test Condition	Test Method	Test Result
Density		ASTM D792/ISO 1183	1.77

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.