PC/ABS CYCOLOY™ CX7240 7M8D043 SABIC INNOVATIVE NANSHA
122
Unit Price:$2797 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 28MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High impact resistance High mobility
- Application Areas:Electrical field Electronic field Architectural application Outdoor applications Engine hood parts Medical supplies Nursing supplies Plastic bag Casters Aerospace Applications Liquid handling
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 15.0 | cm3/10min |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.20 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.10 | % | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.40 到 0.60 | % |
| Melt mass flow rate | 260°C/2.16 kg | ASTM D1238 | 18 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 65.0 | J |
| Tensile modulus | -- 2 | ASTM D638 | 2600 | Mpa |
| -- | ISO 527-2/1 | 2600 | Mpa | |
| tensile strength | Yield 3 | ASTM D638 | 65.0 | Mpa |
| Yield | ISO 527-2/50 | 65.0 | Mpa | |
| Break 3 | ASTM D638 | 58.0 | Mpa | |
| Break | ISO 527-2/50 | 50.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 4.1 | % |
| Yield | ISO 527-2/50 | 4.0 | % | |
| Break 3 | ASTM D638 | 100 | % | |
| Break | ISO 527-2/50 | 90 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2500 | Mpa |
| -- 5 | ISO 178 | 2500 | Mpa | |
| bending strength | -- 5, 6 | ISO 178 | 96.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 104 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ASTM D152511, ISO 306/B5011 | 110 | °C |
| -- | ISO 306/B120 | 113 | °C | |
| thermal conductivity | ISO 8302 | 0.20 | W/m/K | |
| RTI | UL 746 | 90.0 | °C | |
| RTI Imp | UL 746 | 90.0 | °C | |
| RTI Elec | UL 746 | 90.0 | °C | |
| Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 100 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 89.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 99.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10 | ISO 75-2/Af | 93.0 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 7.5E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 7.5E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| Ball Pressure Test | 73 to 77°C | IEC 60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 0.800 mm, in Oil | IEC 60243-1 | 35 | KV/mm |
| 1.60 mm, in Oil | IEC 60243-1 | 25 | KV/mm | |
| 3.20 mm, in Oil | IEC 60243-1 | 17 | KV/mm | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 3 | ||
| Surface resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | > 1.0E+15 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 到 90 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 250 到 300 | °C | ||
| Mold temperature | 60 到 85 | °C | ||
| Hopper temperature | 60 到 80 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Temperature at the rear of the barrel | 230 到 280 | °C | ||
| Temperature in the middle of the barrel | 240 到 290 | °C | ||
| Temperature at the front of the material cylinder | 250 到 300 | °C | ||
| Spray nozzle temperature | 250 到 300 | °C | ||
| Exhaust hole depth | 0.030 到 0.075 | mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 960 | °C |
| 0.75 mm 13 | IEC 60695-2-12 | 960 | °C | |
| Extreme Oxygen Index | ISO 4589-2 | 34 | % | |
| Hot filament ignition temperature | 0.75 mm 13 | IEC 60695-2-13 | 775 | °C |
| 1.0 mm | IEC 60695-2-13 | 825 | °C | |
| 1.5 mm 13 | IEC 60695-2-13 | 775 | °C | |
| 3.0 mm | IEC 60695-2-13 | 800 | °C | |
| 3.0 mm 13 | IEC 60695-2-13 | 775 | °C | |
| UL flame retardant rating | 0.60 mm | UL 94 | V-1 | |
| 0.75 mm | UL 94 | V-0 | ||
| 1.5 mm | UL 94 | 5VB | ||
| 3.0 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.