PC/ABS CYCOLOY™ CX7240-7T1D193 SABIC INNOVATIVE SHANGHAI

125

Unit Price:$4388 USD/MT

Packaging Specification:: 25 KG/PKG

Supply Quantity:: 20MT

Delivery Terms:: FOB

Port of Loading:: China Main Port

Accepted Payment Methods:: T/T

Shipping:: Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Middle flow Chemical resistance Rapid prototyping
Application Areas:Office equipment Electronic and electrical Communication equipment Thin walled products
Color:--
Grade:--

Technical Data Sheet Compare

物理性能	Test Condition	Test Method	Test Result	Unit
收缩率	MD：3.20mm	内部方法	0.40to0.60	%
吸水率	饱和,23°C	ISO62	0.20	%
吸水率	吸水率	平衡,23°C,50%RH	ISO62	0.10	%
熔体体积流动速率	260°C/2.16kg	ISO1133	15.0	cm3/10min
熔体质量流动速率	260°C/2.16kg	ASTMD1238	18	g/10min
密度		ASTMD792	1.19	g/cm³
密度	密度		ISO1183	1.20	g/cm³

机械性能	Test Condition	Test Method	Test Result	Unit
弯曲强度5,		ISO178	96.0	Mpa
装有测量仪表的落镖冲击	23°C,TotalEnergy	ASTMD3763	65.0	J
简支梁缺口冲击强度	-30°C7	ISO179/1eA	10	kJ/m²
	简支梁缺口冲击强度	23°C8	ISO179/1eA	22	kJ/m²
	简支梁缺口冲击强度	简支梁缺口冲击强度	23°C7	ISO179/1eA	20	kJ/m²
悬壁梁缺口冲击强度	-30°C	ASTMD256	180	J/m
	悬壁梁缺口冲击强度	23°C	ASTMD256	700	J/m
		悬壁梁缺口冲击强度	-30°C9	ISO180/1A	10	kJ/m²
			悬壁梁缺口冲击强度	-30°C10	ISO180/1A	10	kJ/m²
				悬壁梁缺口冲击强度	23°C9	ISO180/1A	25	kJ/m²
				悬壁梁缺口冲击强度	悬壁梁缺口冲击强度	23°C10	ISO180/1A	20	kJ/m²
拉伸模量		ASTMD638	2600	Mpa
拉伸模量	拉伸模量		ISO527-2/1	2600	Mpa
拉伸强度	屈服	ASTMD638	65.0	Mpa
	拉伸强度	屈服	ISO527-2/50	65.0	Mpa
		拉伸强度	断裂	ASTMD638	58.0	Mpa
		拉伸强度	拉伸强度	断裂	ISO527-2/50	50.0	Mpa
伸长率	屈服	ASTMD638	4.1	%
	伸长率	屈服	ISO527-2/50	4.0	%
		伸长率	断裂	ASTMD638	100	%
		伸长率	伸长率	断裂	ISO527-2/50	90	%
弯曲模量	50.0mm跨距	ASTMD790	2500	Mpa
弯曲模量	弯曲模量		ISO178	2500	Mpa
弯曲强度	屈服,50.0mm跨距	ASTMD790	104	Mpa

热性能	Test Condition	Test Method	Test Result	Unit
维卡软化点		ASTMD152512	110	°C
	维卡软化点	--	ISO306/B50	110	°C
	维卡软化点	维卡软化点	--	ISO306/B120	113	°C
RTIElec		UL746	90.0	°C
RTIStr		UL746	90.0	°C
导热系数		ISO8302	0.20	W/m/K
RTI Imp		UL746	90.0	°C
热变形温度	0.45MPa,未退火,3.20mm	ASTMD648	100	°C
	热变形温度	1.8MPa,未退火,3.20mm	ASTMD648	89.0	°C
		热变形温度	1.8MPa,未退火,6.40mm	ASTMD648	99.0	°C
		热变形温度	热变形温度	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	93.0	°C
线性热膨胀系数	MD：-40到40°C	ASTME831	7.5E-05	cm/cm/°C
	线性热膨胀系数	MD：-40到40°C	ISO11359-2	7.5E-05	cm/cm/°C
		线性热膨胀系数	TD：-40到40°C	ASTME831	7.5E-05	cm/cm/°C
		线性热膨胀系数	线性热膨胀系数	TD：-40到40°C	ISO11359-2	7.5E-05	cm/cm/°C
Ball Pressure Test	75°C	IEC60695-10-2	Pass

电气性能	Test Condition	Test Method	Test Result	Unit
高电弧燃烧指数	HAI	UL746	PLC0
相比耐漏电起痕指数	CTI	UL746	PLC3
热丝引燃	HWI	UL746	PLC3
介电强度	0.800mm,在油中	IEC60243-1	35	KV/mm
	介电强度	1.60mm,在油中	IEC60243-1	25	KV/mm
	介电强度	介电强度	3.20mm,在油中	IEC60243-1	17	KV/mm
表面电阻率		IEC60093	>1.0E+15	ohms
体积电阻率		IEC60093	>1.0E+15	ohms·cm

可燃性	Test Condition	Test Method	Test Result	Unit
UL阻燃等级	0.60mm	UL94	V-1
	UL阻燃等级	0.75mm	UL94	V-0
		UL阻燃等级	1.5mm	UL94	5VB
		UL阻燃等级	UL阻燃等级	3.0mm	UL94	5VA
灼热丝易燃指数	0.75mm13	IEC60695-2-12	960	°C
灼热丝易燃指数	灼热丝易燃指数	0.75mm	IEC60695-2-12	960	°C
极限氧指数		ISO4589-2	35	%
热灯丝点火温度	0.75mm13	IEC60695-2-13	775	°C
	热灯丝点火温度	1.0mm	IEC60695-2-13	825	°C
		热灯丝点火温度	1.5mm13	IEC60695-2-13	775	°C
			热灯丝点火温度	3.0mm13	IEC60695-2-13	775	°C
			热灯丝点火温度	热灯丝点火温度	3.0mm	IEC60695-2-13	800	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.