PC/ABS CYCOLOY™ XCY620H-1111 SABIC INNOVATIVE NANSHA
147
Unit Price:$2286 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High temperature resistan
- Application Areas:Home appliance components Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.30 | % |
| Saturation,23°C | ISO62 | 0.40 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.13 | % | |
| Melt Volume-Flow Rate (MVR) | 260°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 25.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 40 | kJ/m² |
| 23°C | ISO180/1A | 55 | kJ/m² | |
| Bending stress 3, | ISO178 | 82.0 | Mpa | |
| Impact strength of simply supported beam gap | -30°C | ISO179/1eA | 45 | kJ/m² |
| 23°C | ISO179/1eA | 60 | kJ/m² | |
| CharpyUnnotchedImpactStrength | 23°C | ISO179/1eU | NoBreak | |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 86.0 | Mpa |
| Dart impact equipped with measuring instruments | -30°C,TotalEnergy | ASTMD3763 | 65.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 55.0 | J | |
| Tensile modulus | ISO527-2/1 | 2200 | Mpa | |
| tensile strength | Yield | ISO527-2/50 | 54.0 | Mpa |
| Break | ISO527-2/50 | 56.0 | Mpa | |
| elongation | Yield | ISO527-2/50 | 4.5 | % |
| Break | ISO527-2/50 | 100 | % | |
| Bending modulus | 50.0mmSpan | ASTMD790 | 2300 | Mpa |
| ISO178 | 2200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTMD15259 | 129 | °C | |
| ISO306/B120 | 130 | °C | ||
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 7E-05 | cm/cm/°C | |
| Ball Pressure Test | 75°C | IEC60695-10-2 | Pass | |
| 100°C10 | IEC60695-10-2 | Pass | ||
| Hot deformation temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 106 | °C |
| 0.45MPa,Unannealed,3.20mm | ASTMD648 | 128 | °C | |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 126 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 108 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+16 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+16 | ohms·cm | |
| Dielectric strength | 0.800mm,in Oil | IEC60243-1 | 39 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.