PC/ABS CYCOLAC™ LG9000 BK SABIC INNOVATIVE US
135
Unit Price:$3543 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 38.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance
- Application Areas:Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/5.0 kg | ASTM D1238 | 17 g/10 min |
| Modeling Shrinkage | 流动 : 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.50 到 0.70 % | |
| Moisture Absorption | 24 hr | ASTM D570 | 0.10 % |
| 平衡, 23°C | ASTM D570 | 0.40 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 123 °C |
| 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 129 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 107 °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 110 °C | |
| Vicat Softening Temperature | ASTM D15254 | 129 °C | |
| Linear thermal expansion coefficient | 流动 : -20 到 150°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| 横向 : -20 到 150°C | ASTM E831 | 7.2E-5 cm/cm/°C | |
| Thermal Conductivity | ASTM C177 | 0.20 W/m/K | |
| RTI Elec | UL 746 | 60.0 °C | |
| RTI Imp | UL 746 | 60.0 °C | |
| RTI | UL 746 | 60.0 °C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Gardner | 60°, 无织构 | ASTM D523 | 30 |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Strength | 屈服 | ASTM D638 | 54.0 Mpa |
| Tensile Elongation | 断裂 | ASTM D638 | 75 % |
| Flexural Modulus | 50.0 mm 跨距 | ASTM D790 | 2300 Mpa |
| Flexural Strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 84.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Arc Resistance | ASTM D495 | PLC 6 | |
| Comparative Tracking Index | UL 746 | PLC 2 | |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| Hot-wire Ignition | UL 746 | PLC 2 |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 105 到 110 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.040 % | ||
| Suggested Shot Size | 30 到 80 % | ||
| Rear Temperature | 250 到 290 °C | ||
| Middle Temperature | 255 到 295 °C | ||
| Front Temperature | 260 到 300 °C | ||
| Nozzle Temperature | 275 到 300 °C | ||
| Processing (Melt) Temp | 275 到 300 °C | ||
| Mold Temperature | 60 到 90 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm | ||
| Vent Depth | 0.038 到 0.076 mm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R 级 | ASTM D785 | 118 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Instrumented Dart Impact | -30°C, Total Energy | ASTM D3763 | 33.0 J |
| 23°C, Total Energy | ASTM D3763 | 40.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.