PC/ABS CYCOLAC™ XCY620-100 SABIC INNOVATIVE US
145
Unit Price:$2277 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility｜High temperature resistan
- Application Areas:Home appliance components｜Electrical applications
- Color:--
- Grade:Cold resistant grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 195 Pa·s |
| Melt Mass-Flow Rate | 260°C/5.0kg | ASTMD1238 | 22 g/10min |
| Melt Volume flow Rate | 260°C/5.0kg | ISO1133 | 18.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| TD：3.20mm | 内部方法 | 0.50to0.70 % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.40 % |
| 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 126 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 107 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 105 °C | |
| Vicat Softening Temperature | ASTMD152512 | 127 °C | |
| -- | ISO306/B50 | 127 °C | |
| -- | ISO306/B120 | 129 °C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| Thermal Conductivity | ISO8302 | 0.20 W/m/K |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural Strength | ISO178 | 83.0 Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 89.0 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 55.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 54.0 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 52.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 51.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 4.7 % |
| Tensile Strain | 屈服 | ISO527-2/50 | 4.5 % |
| Tensile Elongation | 断裂 | ASTMD638 | 120 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 120 % |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2300 Mpa |
| ISO178 | 2200 Mpa | ||
| Tensile Modulus | ASTMD638 | 2300 Mpa | |
| ISO527-2/1 | 2200 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dielectric Strength | 3.20mm,在油中 | IEC60243-1 | 17 KV/mm |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dielectric Strength | 0.800mm,在油中 | IEC60243-1 | 35 KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 25 KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Instrumented Dart Impact | -30°C,TotalEnergy | ASTMD3763 | 70.0 J |
| 23°C,TotalEnergy | ASTMD3763 | 56.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.