PC/ABS CYCOLAC™ CX7240 SABIC INNOVATIVE US
169
Unit Price:$4038 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 89.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜High impact resistance｜High mobility
- Application Areas:Electrical field｜Electronic field｜Architectural application｜Outdoor applications｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Casters｜Aerospace Applications｜Liquid handling
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Moisture Absorption | 饱和,23°C | ISO62 | 0.20 % |
| 平衡,23°C,50%RH | ISO62 | 0.10 % | |
| Density / Specific Gravity | ASTMD792 | 1.19 g/cm³ | |
| ISO1183 | 1.20 g/cm³ | ||
| Melt Mass-Flow Rate | 260°C/2.16kg | ASTMD1238 | 18 g/10min |
| Melt Volume flow Rate | 260°C/2.16kg | ISO1133 | 15.0 cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.60 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 100 °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 89.0 °C | |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 99.0 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 93.0 °C | |
| Vicat Softening Temperature | ASTMD152512 | 110 °C | |
| -- | ISO306/B50 | 110 °C | |
| -- | ISO306/B120 | 113 °C | |
| Ball PressureTest | 75°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 7.5E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 7.5E-05 cm/cm/°C | |
| Thermal Conductivity | ISO8302 | 0.20 W/m/K | |
| RTIElec | UL746 | 90.0 °C | |
| Evolution Calendar intelligent importer | UL746 | 90.0 °C | |
| RTIStr | UL746 | 90.0 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 800 °C |
| Oxygen Index | ISO4589-2 | 35 % | |
| Flame Rating | 0.60mm | UL94 | V-1 |
| 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | 5VB | |
| 3.0mm | UL94 | 5VA | |
| Glow Wire Flammability Index | 0.75mm13 | IEC60695-2-12 | 960 °C |
| 0.75mm | IEC60695-2-12 | 960 °C | |
| Glow Wire Ignition Temperature | 0.75mm13 | IEC60695-2-13 | 775 °C |
| 1.0mm | IEC60695-2-13 | 825 °C | |
| 1.5mm13 | IEC60695-2-13 | 775 °C | |
| 3.0mm13 | IEC60695-2-13 | 775 °C |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ASTMD638 | 2600 Mpa | |
| ISO527-2/1 | 2600 Mpa | ||
| Tensile Strength | 屈服 | ASTMD638 | 65.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 65.0 Mpa |
| Tensile Strength | 断裂 | ASTMD638 | 58.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/50 | 50.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 4.1 % |
| Tensile Strain | 屈服 | ISO527-2/50 | 4.0 % |
| Tensile Elongation | 断裂 | ASTMD638 | 100 % |
| Tensile Strain | 断裂 | ISO527-2/50 | 90 % |
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2500 Mpa |
| ISO178 | 2500 Mpa | ||
| Flexural Strength | ISO178 | 96.0 Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 104 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dielectric Strength | 0.800mm,在油中 | IEC60243-1 | 35 KV/mm |
| 1.60mm,在油中 | IEC60243-1 | 25 KV/mm | |
| 3.20mm,在油中 | IEC60243-1 | 17 KV/mm | |
| Comparative Tracking Index | CTI | UL746 | PLC 3 |
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |
| Hot-wire Ignition | HWI | UL746 | PLC 3 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C7 | ISO179/1eA | 10 kJ/m² |
| 23°C8 | ISO179/1eA | 22 kJ/m² | |
| 23°C7 | ISO179/1eA | 20 kJ/m² | |
| Notched Izod Impact Strength | -30°C | ASTMD256 | 180 J/m |
| 23°C | ASTMD256 | 700 J/m | |
| -30°C9 | ISO180/1A | 10 kJ/m² | |
| -30°C10 | ISO180/1A | 10 kJ/m² | |
| 23°C9 | ISO180/1A | 25 kJ/m² | |
| 23°C10 | ISO180/1A | 20 kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 65.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.