PC IUPILON™ KH3520UR MITSUBISHI ENGINEERING JAPAN
156
Unit Price:$9868 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 95.55MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High hardness transparent
- Application Areas:Electric tool casing optical glass
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.17 | ||
| Melt mass flow rate | ASTM D1238/ISO 1133 | 10.5 | g/10min | |
| ASTM D1238/ISO 1133 | 11.5 | g/10min | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.19 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 33 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 2900MPa | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 82.0 | kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 6.0 | % | |
| Rockwell hardness | ASTM D785 | 0.3HRC | ||
| Bending modulus | ASTM D790/ISO 178 | 2900MPa | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 113MPa | kg/cm²(MPa)[Lb/in²] | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 33 | % | |
| Charpy impact strength | ASTM D256/ISO 179 | 200 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 370 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | V-2 | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 123 | ℃（℉） | |
| ASTM D648/ISO 75 | 103 | ℃（℉） |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | ASTM D1003/ISO 13468 | 全光线，透光率89 | % |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dry conditions | 80烘 5-7hr | |||
| Processing temperature | 240-280 | °C | ||
| Mold temperature | 60-80 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.