PC LEXAN™ HFD4271-BK1G103 SABIC INNOVATIVE NANSHA
134
Unit Price:$4139 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50.9MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Hydrolysis resistance
- Application Areas:Electrical applications Automotive Applications Mechanical accessories
- Color:--
- Grade:--
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 流动 : 3.20 mm | 内部方法 | 0.20 到 0.30 | % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.50 | % | |
| 吸水率 | 饱和, 23°C | ISO 62 | 0.13 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.040 | % | |
| 熔体体积流动速率 | 300°C/1.2 kg | ISO 1133 | 14.0 | cm3/10min |
| 熔体质量流动速率 | 300°C/1.2 kg | ASTM D1238 | 15 | g/10 min |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | ASTM D638 | 3700 | Mpa | |
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 1700 | J/m |
| -30°C 6 | ISO 180/1U | 68 | kJ/m² | |
| 23°C 6 | ISO 180/1U | 93 | kJ/m² | |
| 简支梁无缺口冲击强度 | -30°C | ISO 179/1eU | 100 | kJ/m² |
| 23°C | ISO 179/1eU | 110 | kJ/m² | |
| 简支梁缺口冲击强度 | -30°C | ISO 179/1eA | 9.0 | kJ/m² |
| 23°C | ISO 179/1eA | 18 | kJ/m² | |
| 装有测量仪表的落镖冲击 | 23°C, Total Energy | ASTM D3763 | 36.0 | J |
| 拉伸强度 | 屈服 3 | ASTM D638 | 53.0 | Mpa |
| 屈服 | ISO 527-2/5 | 59.0 | Mpa | |
| 断裂 3 | ASTM D638 | 39.0 | Mpa | |
| 断裂 | ISO 527-2/5 | 48.0 | Mpa | |
| 伸长率 | 屈服 3 | ASTM D638 | 3.0 | % |
| 屈服 | ISO 527-2/5 | 3.0 | % | |
| 断裂 | ISO 527-2/5 | 9.0 | % | |
| 弯曲模量 | 50.0 mm 跨距 | ASTM D790 | 3300 | Mpa |
| 弯曲强度 | 屈服, 50.0 mm 跨距 | ASTM D790 | 95.0 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 维卡软化点 | ISO 306/B120 | 135 | °C | |
| 线性热膨胀系数 | 流动 : -40 到 40°C | ASTM E831 | 4.0E-5 | cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 3.0E-5 | cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 7.0E-5 | cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| RTI | UL 746 | 80.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI Elec | UL 746 | 80.0 | °C | |
| 热变形温度 | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 131 | °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 125 | °C | |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥时间 | 3.0 到 4.0 | hr | ||
| 建议注射量 | 40 到 60 | % | ||
| 料筒后部温度 | 265 到 290 | °C | ||
| 料筒中部温度 | 275 到 300 | °C | ||
| 料筒前部温度 | 290 到 310 | °C | ||
| 射嘴温度 | 280 到 305 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 40 到 70 | rpm | ||
| 排气孔深度 | 0.025 到 0.076 | mm | ||
| 干燥温度 | 120 | °C | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 加工（熔体）温度 | 290 到 310 | °C | ||
| 模具温度 | 70 到 95 | °C |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 0.40 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.