PC LEXAN™ CFR9111-NA8G001T SABIC INNOVATIVE NANSHA
63
Unit Price:$4910 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Non chloro non bromine fl
- Application Areas:Electronic and Electrical Plastic bag Lighting applications Electrical appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 300°C/1.2 kg | ISO 1133 | 17.0 | cm3/10min |
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 0.55 到 0.75 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.60 到 0.80 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.13 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.11 | % | |
| Melt mass flow rate | 300°C/1.2 kg | ASTM D1238 | 18 | g/10 min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Non notched cantilever beam impact | -30°C | ASTM D4812, ISO 180/1U | 无断裂 | |
| 23°C | ASTM D4812, ISO 180/1U | 无断裂 | ||
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 80.0 | J |
| Impact strength of simply supported beam gap | -30°C | ISO 179/1eA | 10 | kJ/m² |
| 23°C | ISO 179/1eA | 59 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Tensile modulus | -- 2 | ASTM D638 | 2400 | Mpa |
| -- | ISO 527-2/1 | 2300 | Mpa | |
| tensile strength | Yield 3 | ASTM D638 | 67.0 | Mpa |
| Yield | ISO 527-2/50 | 63.0 | Mpa | |
| Break 3 | ASTM D638 | 54.0 | Mpa | |
| Break | ISO 527-2/50 | 57.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 6.0 | % |
| Yield | ISO 527-2/50 | 6.0 | % | |
| Break 3 | ASTM D638 | 80 | % | |
| Break | ISO 527-2/50 | 73 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2400 | Mpa |
| -- 5 | ISO 178 | 2400 | Mpa | |
| bending strength | -- 5, 6 | ISO 178 | 96.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 103 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ASTM D152510 | 136 | °C |
| -- | ISO 306/B50 | 139 | °C | |
| -- | ISO 306/B120 | 140 | °C | |
| RTI | UL 746 | 130 | °C | |
| RTI Imp | UL 746 | 120 | °C | |
| RTI Elec | UL 746 | 130 | °C | |
| Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 130 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9 | ISO 75-2/Be | 131 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 120 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 9 | ISO 75-2/Ae | 121 | °C | |
| Ball Pressure Test | 123 to 127°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 6.8E-5 | cm/cm/°C |
| Flow : 23 to 80°C | ISO 11359-2 | 7.7E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 7.0E-5 | cm/cm/°C | |
| Across Flow : 23 to 80°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 1.10 GHz | ASTM ES7-83 | 5.6E-3 | |
| Dielectric constant | 1.10 GHz | ASTM ES7-83 | 2.79 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Processing (melt) temperature | 280 到 305 | °C | ||
| Mold temperature | 70 到 95 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 260 到 280 | °C | ||
| Temperature in the middle of the barrel | 270 到 295 | °C | ||
| Temperature at the front of the material cylinder | 280 到 305 | °C | ||
| Spray nozzle temperature | 275 到 300 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Light transmittance | 1000 µm | 内部方法 | > 90.0 | % |
| 2000 µm | 内部方法 | > 89.0 | % | |
| 3000 µm | 内部方法 | > 88.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 1.5 mm | IEC 60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.5 mm | IEC 60695-2-13 | 850 | °C |
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 | |
| 1.2 mm | UL 94 | V-1 | ||
| 1.5 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.