Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜Toughening｜UV resistance
- Application Areas:food｜Thin walled products｜Casters
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Outdoor Suitability | UL 746C | f1 | |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Modeling Shrinkage | 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.35 % |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| Modeling Shrinkage | 流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Density / Specific Gravity | -- | ASTM D792 | 1.18 g/cm³ |
| -- | ISO 1183 | 1.19 g/cm³ |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 115 °C | |
| RTI Elec | UL 746 | 125 °C | |
| Linear thermal expansion coefficient | 横向 : 23 到 80°C | ISO 11359-2 | 7.7E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 6.7E-5 cm/cm/°C | |
| 流动 : -40 到 40°C | ASTM E831 | 6.7E-5 cm/cm/°C | |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Vicat Softening Temperature | -- | ISO 306/B50 | 140 °C |
| -- | ASTM D152512, ISO 306/B12012 | 142 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Ae | 124 °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 124 °C | |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Be | 135 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 120 °C | |
| 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 134 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Oxygen Index | ISO 4589-2 | 35 % | |
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 825 °C |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 3.0 mm | UL 94 | 5VA |
| 1.5 mm | UL 94 | V-0 |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot-wire Ignition | UL 746 | PLC 1 | |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| Comparative Tracking Index | IEC 60112 | 225 V | |
| Dissipation Factor? | 60 Hz | IEC 60250 | 1.0E-3 |
| Comparative Tracking Index | UL 746 | PLC 3 | |
| Dissipation Factor? | 50 Hz | IEC 60250 | 1.0E-3 |
| 60 Hz | ASTM D150 | 2.4E-3 | |
| 1 MHz | ASTM D150, IEC 60250 | 8.5E-3 | |
| 50 Hz | ASTM D150 | 2.4E-3 | |
| Dielectric Constant | 1 MHz | IEC 60250 | 2.70 |
| 60 Hz | IEC 60250 | 2.60 | |
| 50 Hz | IEC 60250 | 2.60 | |
| 1 MHz | ASTM D150 | 2.90 | |
| 50 kHz | ASTM D150 | 2.95 | |
| 60 Hz | ASTM D150 | 2.95 | |
| Dielectric Strength | 3.20 mm, 在油中 | IEC 60243-1 | 16 KV/mm |
| 3.20 mm, in Oil | ASTM D149 | 17 KV/mm | |
| Volume Resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2100 Mpa |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 130 % |
| 断裂 3 | ASTM D638 | 130 % | |
| 屈服 3 | ASTM D638 | 6.0 % | |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| Tensile Strength | 断裂 3 | ASTM D638 | 61.0 Mpa |
| 断裂 | ISO 527-2/50 | 60.0 Mpa | |
| 屈服 3 | ASTM D638 | 58.0 Mpa | |
| 屈服 | ISO 527-2/50 | 55.0 Mpa | |
| Tensile Modulus | -- | ISO 527-2/1 | 2100 Mpa |
| Flexural Modulus | -- 5 | ISO 178 | 2200 Mpa |
| Flexural Stress | -- 5, 6 | ISO 178 | 85.0 Mpa |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2060 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 88.0 Mpa |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vent Depth | 0.025 到 0.076 mm | ||
| Screw Speed | 40 到 70 rpm | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Front Temperature | 295 到 315 °C | ||
| Nozzle Temperature | 290 到 310 °C | ||
| Processing (Melt) Temp | 295 到 315 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Middle Temperature | 280 到 305 °C | ||
| Rear Temperature | 215 到 295 °C | ||
| Suggested Shot Size | 40 到 60 % | ||
| Suggested Max Moisture | 0.020 % | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Drying Temperature | 120 °C |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 90.0 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 60 kJ/m² |
| 23°C | ISO 179/1eA | 75 kJ/m² | |
| Notched Izod Impact Strength | 23°C 8 | 内部方法 | 1100 J/m |
| -30°C | ASTM D256 | 680 J/m | |
| 23°C | ASTM D256 | 800 J/m | |
| -50°C | ASTM D256 | 590 J/m | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 52.0 J |
| Unnotched Izod Impact Strength | 23°C | ISO 180/1U | 无断裂 |
| -30°C | ISO 180/1U | 无断裂 | |
| Notched Izod Impact Strength | 23°C 9 | ISO 180/1A | 70 kJ/m² |
| 23°C 10 | ISO 180/4A | 80 kJ/m² | |
| -30°C 10 | ISO 180/4A | 65 kJ/m² | |
| 23°C, 6.40 mm | ASTM D256 | 640 J/m | |
| -30°C 9 | ISO 180/1A | 55 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.