PC LEXAN™ DMX1435-GY6E563T SABIC INNOVATIVE US
127
Unit Price:$8671 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Scratch resistant｜High temperature resistan｜high strength
- Application Areas:Electronic and electrical｜Automotive components｜Wire and cable
- Color:--
- Grade:--
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| proportion | ASTM D792 | 1.2 g/cm³ | |
| ISO 1183 | 1.17 g/cm³ | ||
| Modeling Shrinkage | 流动3.2mm | 内部测试方法 | 0.5-0.8 % |
| Moisture Absorption | 24hr | ASTM D570 | 0.08 % |
| 23℃平衡 | ASTM D570 | 0.28 % | |
| 50RH平衡 | ASTM D570 | 0.13 % | |
| 50RH 24hr | ASTM D570 | 0.04 % | |
| 23℃饱和 | ISO 62 | 0.27 % | |
| 23℃ 50RH | ISO 62 | 0.13 % | |
| Melt index | 300℃ 1.2kg | ASTM D1238 | 14.5 g/10min |
| 300℃ 1.2kg | ISO 1133 | 13 cm3/10min | |
| Specific Volume | ASTM D792 | 0.85 cm³/g |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 未退火0.45MPa 3.2mm | ASTM D648 | 133 °C |
| 未退火1.8MPa 3.2mm | ASTM D648 | 119 °C | |
| 0.45MPa 4.0mm | ISO 75 | 131 °C | |
| 1.8MPa 4.0mm | ISO 75 | 118 °C | |
| Vicat Softening Temperature | 50℃/hr 50N | ASTM DI 525 | 139 °C |
| 50℃/hr 50N | ISO 306 | 138 °C | |
| 120℃/hr 50N | ISO 306 | 140 °C | |
| Coefficient of Linear Thermal Expansion (Flow) | -40.0~95℃ | ASTM E831 | 0.000070 cm/cm/℃ |
| Coefficient of Linear Thermal Expansion | -40.0~95℃ | ASTM E831 | 0.000070 cm/cm/℃ |
| 流动23~80℃ | ISO 11359 | 0.000070 cm/cm/℃ | |
| 垂直23~80℃ | ISO 11359 | 0.000070 cm/cm/℃ | |
| Thermal Conductivity | ASTM C177 | 0.2 w/(m.℃) | |
| ISO 8302 | 0.2 w/(m.℃) | ||
| Specific Heat | ASTM C351 | 1.4 J/(g.℃) | |
| Ball Indentation Hardness | IEC 60695 | 125 °C | |
| IEC 60695 | 140 °C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Transmittance | 2540pm | ASTM DI 003 | 88 % |
| Haze | 2540Pm | ASTM D1003 | 0.8 % |
| Index of Refraction | ASTM D542 | 1.584 | |
| ISO 489 | 1.584 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | 50mm/min | ASTM D638 | 2900 Mpa |
| 1.0mm/min | ISO 527 | 2450 Mpa | |
| Tensile Strength | 屈服50mm/min I型 | ASTM D638 | 80 Mpa |
| 断裂50mm/mini型 | ASTM D638 | 65 Mpa | |
| 屈服50mm/min | ISO 527 | 80 Mpa | |
| 斯裂50mm/min | ISO 527 | 60 Mpa | |
| Tensile Elongation | 屈服50mm/min iI型 | ASTM D638 | 7 % |
| 断裂50mm/min I型 | ASTM D638 | 70 % | |
| 屈服50mm/min | ISO 527 | 7 % | |
| 断裂50mm/min | ISO 527 | 40 % | |
| Flexural Strength | 屈服1.3mm/min | ASTM D790 | 120 Mpa |
| 屈服2.0mm/min | ISO 178 | 108 Mpa | |
| Flexural Modulus | 1.3mm/min | ASTM D790 | 2600 Mpa |
| 2.0mm/min | ISO 178 | 2450 Mpa | |
| Notched Izod Impact Strength | 23℃ | ASTM D256 | 30 J/m |
| -30℃ | ASTM D256 | 30 J/m | |
| 23°C 3.0mm A型缺口 | ISO 180 | 5 kJ/m² | |
| “-30℃ 3.0mm A型缺口 | ISO 180 | 4 kJ/m² | |
| Unnotched Izod Impact Strength | 23℃ | ASTM D4812 | NB J/m |
| 23°C 3.0mm | ISO 180 | NB kJ/m² | |
| -30℃ 3.0mm | ISO 180 | 45 kJ/m² | |
| Charpy Notched Impact Strength | 23°C3.0mm 1eA型 | ISO 179 | 3 kJ/m² |
| 30℃ 3.0mm 1eA型^ | ISO 179 | 3 kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C 3.0mm | ISO 179 | NB kJ/m² |
| -30℃ 3.0mm | ISO 179 | 47 kJ/m² | |
| Taber Abrasion Resistance | CS-17轮1kg | ASTM D1044 | 10 mg/1000cy |
| CS-17轮1kg | 内部测试方法 | 10 mg/1000cy | |
| ericksen scratch depth | 6N | 内部测试方法 | 14 micrometer |
| Instrumented Dart Impact | 23℃总能量 | ASTM D3763 | 30 J |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | L标尺 | ASTM D785 | 108 |
| M标尺 | ASTM D785 | 93 | |
| Pencil Hardness | 1.0kg | ASTM D3363 | H |
| Ball Indentation Hardness | H358/30 | ISO 2039 | 128 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.