PC Makrolon® 8025 000000 COVESTRO SHANGHAI
198
Unit Price:$3408 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High mobility Filler: Glass fiber with 20% filler by weight 20% filler by weight
- Application Areas:Automotive Applications Lighting installation electrical equipment
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 密度 | 23°C | ISO1183 | 1.34 | g/cm³ |
| 表观密度 | ISO60 | 0.69 | g/cm³ | |
| 熔体质量流动速率 | 300°C/1.2kg | ISO1133 | 6.5 | g/10min |
| 熔体体积流动速率 | 300°C/1.2kg | ISO1133 | 6.00 | cm3/10min |
| 收缩率 | TD | ISO2577 | 0.30to0.45 | % |
| MD | ISO2577 | 0.30to0.45 | % | |
| TD:2.00mm3 | ISO294-4 | 0.35 | % | |
| MD:2.00mm3 | ISO294-4 | 0.55 | % | |
| 吸水率 | 饱和,23°C | ISO62 | 0.24 | % |
| 平衡,23°C,50%RH | ISO62 | 0.10 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | 23°C | ISO527-2/1 | 4000 | Mpa |
| 拉伸强度 | 屈服,23°C | ISO527-2/50 | 58.0 | Mpa |
| 断裂,23°C | ISO527-2/5 | 50.0 | Mpa | |
| 简支梁无缺口冲击强度 | -30°C,完全断裂 | ISO179/1eU | 65 | kJ/m² |
| 23°C,完全断裂 | ISO179/1eU | 55 | kJ/m² | |
| NotchedIzodImpactStrength | 23°C,CompleteBreak | ISO7391 | 12 | kJ/m² |
| 多轴向仪器化冲击能量 | -30°C | ISO6603-2 | 10.0 | J |
| 23°C | ISO6603-2 | 20.0 | J | |
| 多轴向仪器化冲击力峰值 | -30°C | ISO6603-2 | 2800 | N |
| 23°C | ISO6603-2 | 3300 | N | |
| 球压硬度 | ISO2039-1 | 136 | Mpa | |
| 伸长率 | 屈服,23°C | ISO527-2/50 | 3.5 | % |
| 断裂,23°C | ISO527-2/5 | 6.5 | % | |
| TensileCreepModulus | 1hr | ISO899-1 | 3700 | Mpa |
| 拉伸蠕变模量 | 1000hr | ISO899-1 | 3500 | Mpa |
| 弯曲模量 | 23°C | ISO178 | 3700 | Mpa |
| 弯曲强度 | 3.5%Strain,23°C | ISO178 | 95.0 | Mpa |
| 23°C | ISO178 | 100 | Mpa | |
| 弯曲应变 | 23°C | ISO178 | 5.4 | % |
| CharpyNotchedImpactStrength | 23°C,CompleteBreak | ISO7391 | 12 | kJ/m² |
| 简支梁无缺口冲击强度 | -60°C,CompleteBreak | ISO179/1eU | 65 | kJ/m² |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 维卡软化点 | -- | ISO306/B50 | 146 | °C |
| -- | ISO306/B120 | 147 | °C | |
| Ball Pressure Test | 137°C | IEC60695-10-2 | Pass | |
| 线性热膨胀系数 | MD：23到55°C | ISO11359-2 | 4.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 5.5E-05 | cm/cm/°C | |
| 导热系数 | 23°C | ISO8302 | 0.23 | W/m/K |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTI Imp | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 141 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 134 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 体积电阻率 | 23°C | IEC60093 | 1E+16 | ohms·cm |
| 介电强度 | 23°C,1.00mm | IEC60243-1 | 36 | KV/mm |
| 相对电容率 | 23°C,100Hz | IEC60250 | 3.30 | |
| 23°C,1MHz | IEC60250 | 3.30 | ||
| 耗散因数 | 23°C,100Hz | IEC60250 | 1E-03 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| 漏电起痕指数 | 解决方案A | IEC60112 | 175 | V |
| 解决方案B | IEC60112 | 125 | V | |
| 表面电阻率 | IEC60093 | 1E+16 | ohms |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL阻燃等级 | 1.5mm | UL94 | V-2 | |
| 6.0mm | UL94 | V-1 | ||
| 灼热丝易燃指数 | 0.75mm | IEC60695-2-12 | 800 | °C |
| 1.5mm | IEC60695-2-12 | 960 | °C | |
| 2.0mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| 4.0mm | IEC60695-2-12 | 960 | °C | |
| 热灯丝点火温度 | 0.75mm | IEC60695-2-13 | 850 | °C |
| 2.0mm | IEC60695-2-13 | 875 | °C | |
| 3.0mm | IEC60695-2-13 | 875 | °C | |
| 极限氧指数 | ISO4589-2 | 32 | % | |
| ApplicationofFlamefromSmallBurner-MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 | |
| 燃烧速率-US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 470 | °C | |
| 针焰试验 | MethodF:1.50mm | IEC60695-11-5 | 2.0 | min |
| MethodF:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodF:3.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:1.50mm | IEC60695-11-5 | 1.0 | min | |
| MethodK:2.00mm | IEC60695-11-5 | 1.0 | min | |
| MethodK:3.00mm | IEC60695-11-5 | 2.0 | min | |
| SelfIgnitionTemperature | ASTMD1929 | 550 | °C |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISOShortname |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.