PC LNP™ LUBRILOY™ D20001-BK8833 SABIC INNOVATIVE NANSHA
116
Unit Price:$12093 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant
- Application Areas:Electrical appliances Plastic bag Aerospace Applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 流动 : 24小时 | ASTM D955 | 0.70 到 0.90 | % |
| 横向流动 : 24小时 | ASTM D955 | 0.70 到 0.90 | % | |
| 横向流量 : 24小时 | ISO 294-4 | 0.70 到 0.90 | % | |
| 流量 : 24小时 | ISO 294-4 | 0.70 到 0.90 | % | |
| 吸水率 | 24 hr, 50% RH | ASTM D570 | 0.14 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.18 | % | |
| 熔体体积流动速率 | 300°C/1.2 kg | ASTM D1238 | 15.7 | cm3/10min |
| 收缩率 | 流动 : 24小时 | ASTM D955 | 0.50 | % |
| 横向流动 : 24小时 | ASTM D955 | 0.60 | % | |
| 横向流量 : 24小时 | ISO 294-4 | 0.57 | % | |
| 流量 : 24小时 | ISO 294-4 | 0.53 | % | |
| 吸水率 | 平衡, 23°C, 50% RH | ISO 62 | 0.12 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | -- 2 | ASTM D638 | 2550 | Mpa |
| -- | ISO 527-2/1 | 2600 | Mpa | |
| 拉伸强度 | 屈服 | ASTM D638 | 67.0 | Mpa |
| 屈服 | ISO 527-2 | 62.0 | Mpa | |
| 伸长率 | 屈服 | ASTM D638 | 4.5 | % |
| 屈服 | ISO 527-2 | 4.3 | % | |
| 断裂 | ASTM D638 | 6.5 | % | |
| 断裂 | ISO 527-2 | 6.7 | % | |
| 弯曲模量 | -- | ASTM D790 | 2820 | Mpa |
| -- | ISO 178 | 2800 | Mpa | |
| 弯曲强度 | -- | ASTM D790 | 103 | Mpa |
| -- | ISO 178 | 102 | Mpa | |
| 摩擦系数 | Dynamic | ASTM D3702 | 0.090 | |
| Static | ASTM D3702 | 0.22 | ||
| 磨损因数 | ASTM D3702 | 6.0E+6 | 10^-8 mm³/N·m | |
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 1600 | J/m |
| 23°C 4 | ISO 180/1U | 100 | kJ/m² | |
| 装有测量仪表的落镖冲击 | 23°C, Energy at Peak | ASTM D3763 | 51.0 | J |
| 拉伸模量 | -- 2 | ASTM D638 | 1860 | Mpa |
| -- | ISO 527-2/1 | 2120 | Mpa | |
| 拉伸强度 | 屈服 | ASTM D638 | 53.0 | Mpa |
| 屈服 | ISO 527-2 | 51.0 | Mpa | |
| 断裂 | ASTM D638 | 60.0 | Mpa | |
| 断裂 | ISO 527-2 | 54.0 | Mpa | |
| 伸长率 | 屈服 | ASTM D638 | 6.5 | % |
| 屈服 | ISO 527-2 | 5.6 | % | |
| 断裂 | ASTM D638 | 130 | % | |
| 断裂 | ISO 527-2 | 99 | % | |
| 弯曲模量 | ASTM D790, ISO 178 | 2130 | Mpa | |
| 弯曲强度 | -- | ASTM D790 | 82.0 | Mpa |
| -- | ISO 178 | 78.0 | Mpa | |
| 摩擦系数 | Dynamic | ASTM D3702 | 0.16 | |
| Static | ASTM D3702 | 0.090 | ||
| 磨损因数 | ASTM D3702 | 1.2E+7 | 10^-8 mm³/N·m | |
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 无断裂 | |
| 23°C 4 | ISO 180/1U | 140 | kJ/m² | |
| 装有测量仪表的落镖冲击 | 23°C, Energy at Peak | ASTM D3763 | 40.0 | J |
| -- | ISO 6603-2 | 45.0 | J |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 142 | °C |
| 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 4 | ISO 75-2/Bf | 140 | °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 130 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 4 | ISO 75-2/Af | 128 | °C | |
| 线性热膨胀系数 | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 7.4E-5 | cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 7.4E-5 | cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 7.4E-5 | cm/cm/°C | |
| 热变形温度 | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 97.0 | °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 89.0 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 4 | ISO 75-2/Af | 94.0 | °C | |
| 线性热膨胀系数 | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 6.6E-5 | cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 6.7E-5 | cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 6.7E-5 | cm/cm/°C |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 80 | °C | ||
| 干燥时间 | 4.0 到 6.0 | hr | ||
| 料筒后部温度 | 250 到 260 | °C | ||
| 料筒中部温度 | 255 到 265 | °C | ||
| 料筒前部温度 | 260 到 270 | °C | ||
| 加工（熔体）温度 | 255 到 290 | °C | ||
| 模具温度 | 40 到 65 | °C | ||
| 干燥温度 | 100 | °C | ||
| 干燥时间 | 4.0 | hr | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 料筒后部温度 | 295 到 305 | °C | ||
| 料筒中部温度 | 300 到 310 | °C | ||
| 料筒前部温度 | 305 到 315 | °C | ||
| 加工（熔体）温度 | 305 到 315 | °C | ||
| 模具温度 | 65 到 95 | °C | ||
| 背压 | 0.200 到 0.300 | Mpa | ||
| 螺杆转速 | 30 到 60 | rpm |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 1.5 mm, Testing by SABIC | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.