PC LEXAN™ LUX9616-WH5E140X SABIC INNOVATIVE US
106
Unit Price:$4380 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 28MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜transparent｜optical performance ｜Thermal stability
- Application Areas:Plastic bag｜Lighting applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 7.0 g/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.60到0.80 % |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat Softening Temperature | ASTMD152513 | 141 °C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 6.8E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 6.7E-05 cm/cm/°C | |
| 0.45MPa, Unannealed,3.20mm Span | ISO75-2/Bf | 135 °C | |
| 1.8MPa, Unannealed,3.20mm | ASTMD648 | 125 °C | |
| 1.8MPa, Unannealed,64.0mm Span | ISO75-2/Af | 125 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.50mm | IEC60695-2-13 | 850 °C |
| Flame Rating | 1.50mm | UL94 | V-0 |
| Glow Wire Flammability Index | 1.00mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.00mm | IEC60695-2-13 | 850 °C |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 50.0mm Span | ASTMD790 | 2160 Mpa | |
| --7 | ISO178 | 2250 Mpa | |
| --8 | ISO178 | 95.0 Mpa | |
| --1 | ASTMD638 | 2300 Mpa | |
| Yield | ASTMD638 | 62.0 Mpa | |
| yield | ISO527-2/50 | 62.0 Mpa | |
| Break | ASTMD638 | 65.0 Mpa | |
| fracture | ISO527-2/50 | 58.0 Mpa | |
| Yield | ASTMD638 | 6.0 % | |
| yield | ISO527-2/50 | 6.0 % | |
| Break | ASTMD638 | 80 % | |
| fracture | ISO527-2/50 | 75 % | |
| Yield,50.0mm Span | ASTMD790 | 95.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Comparative Tracking Index | CTI | UL746 | PLC 3 |
| High Amp Arc Ignition | HAI | UL746 | PLC 1 |
| Hot-wire Ignition | HWI | UL746 | PLC 3 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23°C | ASTMD256 | 150 J/m | |
| 23°C10 | ISO180/1A | 15 kJ/m² | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 70.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.