PC LEXAN™ EXL1414-BR6G119 SABIC INNOVATIVE US
123
Unit Price:$3248 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Processability｜Moderate liquidity｜Ductility｜copolymer｜Good demolding performanc
- Application Areas:Home appliance components｜Electronic Applications｜Bottle cap
- Color:--
- Grade:--
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density / Specific Gravity | -- | ISO 1183 | 1.19 g/cm³ |
| -- | ASTM D792 | 1.18 g/cm³ | |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| 饱和, 23°C | ISO 62 | 0.35 % | |
| Modeling Shrinkage | 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| 流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI | UL 746 | 125 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Elec | UL 746 | 130 °C | |
| Linear thermal expansion coefficient | 横向 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C | |
| 流动 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C | |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Vicat Softening Temperature | -- | ASTM D152510, ISO 306/B5010 | 145 °C |
| -- | ISO 306/B120 | 146 °C | |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 128 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 124 °C | |
| 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 139 °C | |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Be | 140 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 875 °C |
| 3.0 mm | IEC 60695-2-13 | 875 °C | |
| Glow Wire Flammability Index | 0.8 mm | IEC 60695-2-12 | 850 °C |
| 1.0 mm | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 0.40 mm | UL 94 | HB |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor? | 1 MHz | ASTM D150 | 9.3E-3 |
| 100 Hz | ASTM D150 | 1.2E-3 | |
| Dielectric Constant | 1 MHz | ASTM D150 | 2.64 |
| 100 Hz | ASTM D150 | 2.68 | |
| Dielectric Strength | 0.800 mm, in Oil | ASTM D149 | 16 KV/mm |
| Volume Resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2230 Mpa |
| Tensile Elongation | 断裂 3 | ASTM D638 | 98 % |
| 断裂 | ISO 527-2/50 | 120 % | |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| 屈服 3 | ASTM D638 | 6.0 % | |
| Tensile Strength | 断裂 | ISO 527-2/50 | 60.0 Mpa |
| 断裂 3 | ASTM D638 | 50.0 Mpa | |
| 屈服 | ISO 527-2/50 | 57.0 Mpa | |
| 屈服 3 | ASTM D638 | 55.0 Mpa | |
| Tensile Modulus | -- 2 | ASTM D638 | 2020 Mpa |
| -- | ISO 527-2/1 | 2150 Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 85.0 Mpa |
| Flexural Modulus | -- 5 | ISO 178 | 2250 Mpa |
| Flexural Stress | 屈服, 50.0 mm 跨距 4 | ASTM D790 | 92.0 Mpa |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vent Depth | 0.025 到 0.076 mm | ||
| Screw Speed | 40 到 70 rpm | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Mold Temperature | 70 到 95 °C | ||
| Processing (Melt) Temp | 295 到 315 °C | ||
| Nozzle Temperature | 290 到 310 °C | ||
| Suggested Shot Size | 40 到 60 % | ||
| Rear Temperature | 270 到 295 °C | ||
| Middle Temperature | 280 到 305 °C | ||
| Front Temperature | 295 到 315 °C | ||
| Suggested Max Moisture | 0.020 % | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Drying Temperature | 120 °C |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R 级 | ASTM D785 | 121 |
| L 计秤 | ASTM D785 | 89 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 kJ/m² |
| Notched Izod Impact Strength | 23°C | ASTM D256 | 870 J/m |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 无断裂 |
| Notched Izod Impact Strength | -30°C | ASTM D256 | 770 J/m |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| Notched Izod Impact Strength | -30°C 8 | ISO 180/1A | 60 kJ/m² |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 70.0 J |
| Notched Izod Impact Strength | 23°C 8 | ISO 180/1A | 70 kJ/m² |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 |
| 23°C | ISO 180/1U | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.