PC LEXAN™ EXL9330 2R2D017 SABIC INNOVATIVE NANSHA
95
Unit Price:$4710 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 33MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜Toughening｜UV resistance
- Application Areas:Casters｜Thin walled products｜food
- Color:--
- Grade:--
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density / Specific Gravity | -- | ASTM D792 | 1.18 g/cm³ |
| -- | ISO 1183 | 1.19 g/cm³ | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| Modeling Shrinkage | 流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.35 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.15 % | |
| Outdoor Suitability | UL 746C | f1 |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 134 °C |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Be | 135 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 120 °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 124 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Ae | 124 °C | |
| Vicat Softening Temperature | -- | ASTM D152512, ISO 306/B12012 | 142 °C |
| -- | ISO 306/B50 | 140 °C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 6.7E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 6.7E-5 cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.7E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 125 °C | |
| RTI Imp | UL 746 | 115 °C | |
| RTI | UL 746 | 120 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| 3.0 mm | UL 94 | 5VA | |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 825 °C |
| Oxygen Index | ISO 4589-2 | 35 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2100 Mpa |
| -- | ISO 527-2/1 | 2100 Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 58.0 Mpa |
| 屈服 | ISO 527-2/50 | 55.0 Mpa | |
| 断裂 3 | ASTM D638 | 61.0 Mpa | |
| 断裂 | ISO 527-2/50 | 60.0 Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 6.0 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| 断裂 3 | ASTM D638 | 130 % | |
| 断裂 | ISO 527-2/50 | 130 % | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2060 Mpa |
| -- 5 | ISO 178 | 2200 Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 85.0 Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 88.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume Resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Dielectric Strength | 3.20 mm, in Oil | ASTM D149 | 17 KV/mm |
| 3.20 mm, 在油中 | IEC 60243-1 | 16 KV/mm | |
| Dielectric Constant | 60 Hz | ASTM D150 | 2.95 |
| 50 kHz | ASTM D150 | 2.95 | |
| 1 MHz | ASTM D150 | 2.90 | |
| 50 Hz | IEC 60250 | 2.60 | |
| 60 Hz | IEC 60250 | 2.60 | |
| 1 MHz | IEC 60250 | 2.70 | |
| Dissipation Factor? | 50 Hz | ASTM D150 | 2.4E-3 |
| 60 Hz | ASTM D150 | 2.4E-3 | |
| 1 MHz | ASTM D150, IEC 60250 | 8.5E-3 | |
| 50 Hz | IEC 60250 | 1.0E-3 | |
| 60 Hz | IEC 60250 | 1.0E-3 | |
| Comparative Tracking Index | UL 746 | PLC 3 | |
| IEC 60112 | 225 V | ||
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| Hot-wire Ignition | UL 746 | PLC 1 |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 120 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 40 到 60 % | ||
| Rear Temperature | 215 到 295 °C | ||
| Middle Temperature | 280 到 305 °C | ||
| Front Temperature | 295 到 315 °C | ||
| Nozzle Temperature | 290 到 310 °C | ||
| Processing (Melt) Temp | 295 到 315 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm | ||
| Vent Depth | 0.025 到 0.076 mm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 90.0 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 60 kJ/m² |
| 23°C | ISO 179/1eA | 75 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Notched Izod Impact Strength | -50°C | ASTM D256 | 590 J/m |
| -30°C | ASTM D256 | 680 J/m | |
| 23°C | ASTM D256 | 800 J/m | |
| 23°C 8 | 内部方法 | 1100 J/m | |
| 23°C, 6.40 mm | ASTM D256 | 640 J/m | |
| -30°C 9 | ISO 180/1A | 55 kJ/m² | |
| -30°C 10 | ISO 180/4A | 65 kJ/m² | |
| 23°C 9 | ISO 180/1A | 70 kJ/m² | |
| 23°C 10 | ISO 180/4A | 80 kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 |
| 23°C | ISO 180/1U | 无断裂 | |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 52.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.