PC LUPOY® GP2102-KA02 LG GUANGZHOU
224
Unit Price:$3613 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 70MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Chemical resistance
- Application Areas:Electrical field Electronic field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792 | 1.25 | g/cm³ | |
| Melt mass flow rate | 300°C/1.2 kg | ASTM D1238 | 9.0 | g/10 min |
| Shrinkage rate - flow | 23°C, 3.20 mm, Injection | ASTM D955 | 0.20 到 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale, 23°C, Injection | ASTM D785 | 124 | |
| tensile strength | Yield, 23°C, 3.20 mm, Injection | ASTM D638 | 53.9 | Mpa |
| elongation | Break, 23°C, 3.20 mm, Injection | ASTM D638 | 15 | % |
| Bending modulus | 23°C, 3.20 mm, Injection | ASTM D790 | 3330 | Mpa |
| bending strength | 23°C, 3.20 mm, Injection | ASTM D790 | 98.1 | Mpa |
| Impact strength of cantilever beam gap | 23°C, 3.20 mm, Injection | ASTM D256 | 270 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed, 6.40 mm, Injection | ASTM D648 | 137 | °C |
| RTI Elec | UL 746 | 80.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI | UL 746 | 80.0 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 100 到 120 | °C | ||
| drying time | 3.0 到 5.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Minimum Moisture Content | 0.020 | % | ||
| Temperature at the rear of the barrel | 280 到 295 | °C | ||
| Temperature in the middle of the barrel | 285 到 300 | °C | ||
| Temperature at the front of the material cylinder | 290 到 305 | °C | ||
| Spray nozzle temperature | 290 到 305 | °C | ||
| Processing (melt) temperature | 295 到 310 | °C | ||
| Mold temperature | 90 到 110 | °C | ||
| Back pressure | 0.981 到 3.92 | Mpa | ||
| Screw speed | 40 到 70 | rpm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.