PC LEXAN™ HFD4412 BK1E808 SABIC INNOVATIVE NANSHA
103
Unit Price:$2547 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 22MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:Architectural Application｜Plastic bag
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 15 g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 14.0 cm3/10min |
| Modeling Shrinkage | 流动 : 3.20 mm | 内部方法 | 0.10 到 0.30 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.10 到 0.30 % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.30 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.12 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 130 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 125 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7 | ISO 75-2/Af | 127 °C | |
| Vicat Softening Temperature | ISO 306/B120 | 143 °C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 3.0E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 3.0E-5 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 80.0 °C | |
| RTI Imp | UL 746 | 80.0 °C | |
| RTI | UL 746 | 80.0 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.30 mm | UL 94 | HB |
| Glow Wire Flammability Index | 2.0 mm | IEC 60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 850 °C |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | 6400 Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 96.0 Mpa |
| 屈服 | ISO 527-2/5 | 110 Mpa | |
| 断裂 3 | ASTM D638 | 96.0 Mpa | |
| 断裂 | ISO 527-2/5 | 110 Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 3.0 % |
| 屈服 | ISO 527-2/5 | 2.8 % | |
| 断裂 | ISO 527-2/5 | 2.7 % | |
| Flexural Modulus | 50.0 mm 跨距 | ASTM D790 | 5850 Mpa |
| Flexural Strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 159 Mpa |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 120 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 40 到 60 % | ||
| Rear Temperature | 265 到 290 °C | ||
| Middle Temperature | 275 到 300 °C | ||
| Front Temperature | 290 到 310 °C | ||
| Nozzle Temperature | 280 到 305 °C | ||
| Processing (Melt) Temp | 290 到 310 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm | ||
| Vent Depth | 0.025 到 0.076 mm |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 8.0 kJ/m² |
| 23°C | ISO 179/1eA | 8.0 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 48 kJ/m² |
| 23°C | ISO 179/1eU | 43 kJ/m² | |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 830 J/m |
| -30°C 6 | ISO 180/1U | 40 kJ/m² | |
| 23°C 6 | ISO 180/1U | 42 kJ/m² | |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 21.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.