PC Makrolon® AL2447 350392 COVESTRO GERMANY
161
Unit Price:$6929 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low viscosity
- Application Areas:Automotive Applications Electrical applications Industrial applications
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 19.0 | cm3/10min |
| Shrinkage rate | TD | ISO2577 | 0.50到0.70 | % |
| MD | ISO2577 | 0.50到0.70 | % | |
| TD:2.00mm4 | ISO294-4 | 0.70 | % | |
| MD:2.00mm4 | ISO294-4 | 0.65 | % | |
| Apparent density | ISO60 | 0.66 | g/cm³ | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 20 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strain | 23°C | ISO178 | 7.0 | % |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 65.0 | J |
| 23°C | ISO6603-2 | 55.0 | J | |
| Tensile creep modulus | 1hr | ISO899-1 | 2200 | Mpa |
| 1000hr | ISO899-1 | 1900 | Mpa | |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | >50 | % |
| Impact strength of simply supported beam gap | -30°C,Complete Break | ISO7391 | 14 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
| Suspended wall beam gap impact strength | -30°C,Complete Break | ISO7391 | 15 | kJ/m² |
| 23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 6000 | N |
| 23°C | ISO6603-2 | 5100 | N | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 无断裂 | |
| -60°C | ISO179/1eU | 无断裂 | ||
| -30°C | ISO179/1eU | 无断裂 | ||
| Ball pressure hardness | ISO2039-1 | 115 | Mpa | |
| Tensile modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
| tensile strength | Yield,23°C | ISO527-2/50 | 66.0 | Mpa |
| Break,23°C | ISO527-2/5 | 70.0 | Mpa | |
| Break,23°C | ISO527-2/50 | 65.0 | Mpa | |
| elongation | Yield,23°C | ISO527-2/50 | 6.0 | % |
| Break,23°C | ISO527-2/5 | 130 | % | |
| Break,23°C | ISO527-2/50 | 120 | % | |
| Bending modulus | 23°C | ISO178 | 2350 | Mpa |
| bending strength | 23°C | ISO178 | 98.0 | Mpa |
| 3.5%Strain,23°C | ISO178 | 74.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ISO306/B50 | 144 | °C |
| -- | ISO306/B120 | 145 | °C | |
| RTI | 1.5mm | UL746 | 125 | °C |
| RTI Imp | 1.5mm | UL746 | 115 | °C |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| Linear coefficient of thermal expansion | MD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
| Thermal conductivity coefficient | 23°C | ISO8302 | 0.20 | W/m/K |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 138 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 125 | °C | |
| Ball Pressure Test | 135°C | IEC60695-10-2 | 通过 | |
| Glass transition temperature | ISO11357-2 | 145 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 23°C,100Hz | IEC60250 | 5E-04 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
| 23°C,1MHz | IEC60250 | 3.00 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 250 | V |
| SolutionB | IEC60112 | 125 | V | |
| Surface resistivity | IEC60093 | 1E+16 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| GasPermeation | CarbonDioxide:23°C,25.4µm | ISO2556 | 18900 | cm³/m²/bar/24hr |
| CarbonDioxide:23°C,100.0µm | ISO2556 | 4800 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,25.4µm | ISO2556 | 630 | cm³/m²/bar/24hr | |
| Nitrogen:23°C,100.0µm | ISO2556 | 160 | cm³/m²/bar/24hr | |
| Oxygen:23°C,25.4µm | ISO2556 | 3150 | cm³/m²/bar/24hr | |
| Oxygen:23°C,100.0µm | ISO2556 | 800 | cm³/m²/bar/24hr | |
| Water vapor permeability | 23°C,85%RH,100µm | ISO15106-1 | 15 | g/m²/24hr |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 3000µm | ISO14782 | <0.50 | % |
| Light transmittance | 1000µm | ISO13468-2 | 89.0 | % |
| 2000µm | ISO13468-2 | 89.0 | % | |
| 3000µm | ISO13468-2 | 88.0 | % | |
| 4000µm | ISO13468-2 | >87.0 | % | |
| Refractive index | ISO489 | 1.586 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlashIgnitionTemperature | ASTMD1929 | 480 | °C | |
| SelfIgnition | ASTMD1929 | 550 | °C | |
| UL flame retardant rating | 2.7mm | UL94 | HB | |
| 0.75mm | UL94 | V-2 | ||
| Extreme Oxygen Index | ISO4589-2 | 28 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ||||
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.