PC LEXAN™ EXL9112-111 SABIC INNOVATIVE SPAIN
140
Unit Price:$3937 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 18MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Ductility at low temperat Short molding cycle
- Application Areas:Electronic and Electrical Plastic bag lens Industrial applications
- Color:--
- Grade:Light diffusion level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.18 | g/cm³ | |
| ISO1183 | 1.19 | g/cm³ | ||
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 17 | g/10min |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 16.0 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| TD：3.20mm | 内部方法 | 0.40to0.80 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.35 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Outdoor applicability | UL746C | f1 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 2270 | Mpa | |
| ISO527-2/1 | 2200 | Mpa | ||
| tensile strength | Yield | ASTMD638 | 58.1 | Mpa |
| Yield | ISO527-2/50 | 59.0 | Mpa | |
| Break | ASTMD638 | 58.5 | Mpa | |
| Break | ISO527-2/50 | 55.0 | Mpa | |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 560 | J/m |
| 23°C | ASTMD256 | 730 | J/m | |
| -30°C8 | ISO180/1A | 18 | kJ/m² | |
| -30°C9 | ISO180/1A | 20 | kJ/m² | |
| 23°C9 | ISO180/1A | 55 | kJ/m² | |
| 23°C8 | ISO180/1A | 53 | kJ/m² | |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 67.9 | J |
| Ball pressure hardness | H358/30 | ISO2039-1 | 95.0 | Mpa |
| elongation | Yield | ASTMD638 | 5.8 | % |
| Yield | ISO527-2/50 | 5.0 | % | |
| Break | ASTMD638 | 100 | % | |
| Break | ISO527-2/50 | 100 | % | |
| Bending modulus | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
| ISO178 | 2300 | Mpa | ||
| Bending strength 5, | ISO178 | 88.0 | Mpa | |
| bending strength | Yield,50.0mmSpan | ASTMD790 | 95.1 | Mpa |
| Impact strength of simply supported beam gap | -30°C | ISO179/1eA | 25 | kJ/m² |
| 23°C | ISO179/1eA | 60 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 136 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 136 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 124 | °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 124 | °C | |
| vicat softening point | ASTMD152511 | 143 | °C | |
| -- | ISO306/B50 | 143 | °C | |
| -- | ISO306/B120 | 144 | °C | |
| Ball Pressure Test | 125°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 7.2E-05 | cm/cm/°C |
| MD：23to80°C | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.2E-05 | cm/cm/°C | |
| TD：23to80°C | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| RTIElec | UL746 | 130 | °C | |
| RTI Imp | UL746 | 120 | °C | |
| RTIStr | UL746 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,in Oil | IEC60243-1 | 19 | KV/mm |
| Relative permittivity | 50Hz | IEC60250 | 2.70 | |
| 60Hz | IEC60250 | 2.70 | ||
| 1MHz | IEC60250 | 2.70 | ||
| Dissipation factor | 50Hz | IEC60250 | 4E-04 | |
| 60Hz | IEC60250 | 4E-04 | ||
| 1MHz | IEC60250 | 0.010 | ||
| Leakage Trace Index | IEC60112 | 175 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | 5VA | ||
| Burning wire flammability index | 1.0mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 825 | °C |
| Extreme Oxygen Index | ISO4589-2 | 40 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.