PC LEXAN™ EXL1413T BK SABIC INNOVATIVE US
123
- Unit Price:$3603 USD/MT
- Packaging Specification:25 KG/PKG
- Supply Quantity:32.7MT
- Delivery Terms:FOB
- Port of Loading:China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:High mobility｜High ductility at low tem｜Short molding cycle
- Application Areas:Casters｜Electrical applications｜Architectural Application｜Plastic bag｜lens
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2 kg | ISO 1133 | 9 cm³/10 min |
| Melt Mass-Flow Rate(300°C/1.2 kg) | / | ASTM D1238 | 10 g/10min |
| Modeling Shrinkage(Across Flow) | 3.2 mm | Internal | 0.4~0.8 |
| Modeling Shrinkage (Across Flow) | 3.2 mm | Internal | 0.4~0.8 |
| Moisture Absorption | 23°C/sat | ISO 62 | 0.12 |
| 23°C / 50 | ISO 62 | 0.09 |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat Softening Temperature | Rate A/ | ASTM D1525 | 141 °C |
| Rate B/1 | ISO 306 | 142 °C | |
| Rate B/1 | ISO 306 | 141 °C | |
| Relative Temperature Index | UL 746B | 120 °C | |
| UL 746B | 130 °C | ||
| UL 746B | 130 °C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Transmittance | 2.54 mm | ASTM D1003 | 82 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Strength(Yield) | Type I, 5 | ASTM D638 | 58 Mpa |
| 50 mm/m | ISO 527 | 57 Mpa | |
| Tensile Strength(Break) | 50 mm/m | ISO 527 | 61 Mpa |
| Type I, 50 | ASTM D638 | 64 Mpa | |
| Tensile Elongation?(Yield) | Type I, 5 | ASTM D638 | 5.8 % |
| 50 mm/m | ISO 527 | 5.5 % | |
| Tensile Elongation?(Break) | Type I, 5 | ASTM D638 | 131.4 % |
| 50 mm/m | ISO 527 | 124.9 % | |
| Tensile Strength(Yield) | 1.3 mm/min/ | ASTM D790 | 94 Mpa |
| 2 mm/ | ISO 178 | 90 Mpa | |
| Flexural Modulus | 2 mm/mi | ISO 178 | 2150 Mpa |
| 1.3 mm/min | ASTM D790 | 2210 Mpa | |
| Tensile Modulus | 50 mm/ | ASTM D638 | 22610 Mpa |
| 1 mm/ | ISO 527 | 2350 Mpa |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | ISO 2039-2 | 89 L |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength (-30°C) | V-notch Edgew | ISO 179/1eA | 60 kJ/m² |
| Charpy Notched Impact Strength (23°C) | V-notch Edgew | ISO 179/1eA | 70 kJ/m² |
| Notched Izod Impact Strength (-30℃ ) | / | ASTM D256 | 795 J/m |
| 80*10*3 | ISO 180/1A | 55 kJ/m² | |
| Notched Izod Impact Strength 23℃ | ASTM D256 | 890 J/m | |
| Notched Izod Impact Strength (23℃) | 80*10*3 | ISO 180/1A | 65 kJ/m² |
| 80*10*3 | ISO 180/1U | NB J/m | |
| Instrumented Dart Impact (-30℃) | 80*10*3 | ASTM D3763 | 85 J |
| Instrumented Dart Impact (23℃) | 80*10*3 | ASTM D3763 | 82 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.