PC LEXAN™ XHT2143 BK1C141 SABIC INNOVATIVE US

237

Unit Price:US$ 5,059 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
51MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility
Application Areas:Lighting applications｜Automotive External Parts｜Architectural Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C, Total Energy	ASTM D3763	68.0 J

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield, 50.0 mm Span4	ASTM D790	110 Mpa
bending strength	bending strength	--5,6	ISO 178	100 Mpa
Bending modulus	--5	ISO 178	2450 Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2550 Mpa
elongation	Break	ISO 527-2/50	90 %
	elongation	Break3	ASTM D638	90 %
		elongation	Yield	ISO 527-2/50	6.5 %
		elongation	elongation	Yield3	ASTM D638	6.5 %
tensile strength	Break	ISO 527-2/50	60.0 Mpa
	tensile strength	Break3	ASTM D638	60.0 Mpa
		tensile strength	Yield	ISO 527-2/50	70.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	70.0 Mpa
Tensile modulus	--	ISO 527-2/1	2600 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2600 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			135 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			270 to 310 °C
Temperature in the middle of the barrel			280 to 320 °C
Temperature at the front of the material cylinder			290 to 330 °C
Spray nozzle temperature			285 to 325 °C
Processing (melt) temperature			290 to 330 °C
Mold temperature			85 to 130 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 90 rpm
Exhaust hole depth			0.025 to 0.080 mm

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/B50	160 °C
	Vicat softening temperature	--	ISO 306/B120	162 °C
	Vicat softening temperature	Vicat softening temperature	--	ASTM D15259	161 °C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	142 °C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	145 °C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	155 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.0E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.0E-5 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.23 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Shrinkage rate	3.20 mm，Flow	Internal Method	0.60 - 0.90 %
Melt Volume Flow Rate (MVR)	330°C/2.16 kg	ISO 1133	43.0 cm3/10min
melt mass-flow rate	330°C/2.16 kg	ASTM D1238	46 g/10 min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LEXAN™ XHT2143 BK1C141 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet