plas
Log In
CategoriesAll
Home
Plastic Raw Materials
PC

PC LEXAN™  XHT3143 NA6D004T SABIC INNOVATIVE US

190
  • Unit Price:US$ 5,842 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    57MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High mobility
  • Application Areas:Lighting applications｜Automotive External Parts｜Architectural Applications
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength23°CISO 179/1eA11 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Dart impact23°C, Total EnergyASTM D376368.0 J
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthYield, 50.0 mm Span4ASTM D790120 Mpa
bending strength--5,6ISO 17880.0 Mpa
Bending modulus--5ISO 1782500 Mpa
Bending modulus50.0 mm Span4ASTM D7902600 Mpa
elongationBreakISO 527-2/5070 %
elongationBreak3ASTM D63870 %
elongationYieldISO 527-2/506.0 %
elongationYield3ASTM D6386.0 %
tensile strengthBreakISO 527-2/5060.0 Mpa
Tensile modulus--ISO 527-2/12500 Mpa
Tensile modulus--2ASTM D6382700 Mpa
tensile strengthBreak3ASTM D63855.0 Mpa
tensile strengthYieldISO 527-2/5070.0 Mpa
tensile strengthYield3ASTM D63870.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature135 °C
drying time4.0 to 6.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel270 to 300 °C
Temperature in the middle of the barrel280 to 310 °C
Temperature at the front of the material cylinder290 to 325 °C
Spray nozzle temperature285 to 320 °C
Processing (melt) temperature290 to 325 °C
Mold temperature95 to 130 °C
Back pressure0.300 to 0.700 Mpa
Screw speed40 to 90 rpm
Exhaust hole depth0.025 to 0.080 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648166 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648156 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af152 °C
Vicat softening temperature--ASTM D152510170 °C
Vicat softening temperature--ISO 306/B50168 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8316.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8316.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-26.0E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.30 %
Water absorption rateSaturation, 23°CISO 620.30 %
Shrinkage rate3.20 mm，FlowInternal Method0.60 - 0.90 %
Melt Volume Flow Rate (MVR)330°C/2.16 kgISO 113330.0 cm3/10min
melt mass-flow rate330°C/2.16 kgASTM D123833 g/10 min
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.