PC LEXAN™ EXL1414-BK10227L SABIC INNOVATIVE US
120
- Unit Price:$2822 USD/MT
- Packaging Specification:25 KG/PKG
- Supply Quantity:31MT
- Delivery Terms:FOB
- Port of Loading:China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Processability｜Moderate liquidity｜Ductility｜copolymer｜Good demolding performanc
- Application Areas:Bottle cap｜Home appliance components｜Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density / Specific Gravity | -- | ASTM D792 | 1.18 g/cm³ |
| -- | ISO 1183 | 1.19 g/cm³ | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 10 g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 9.00 cm3/10min |
| Modeling Shrinkage | 流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.35 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 125 °C | |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 139 °C |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Be | 140 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 124 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 128 °C | |
| Vicat Softening Temperature | -- | ASTM D152510, ISO 306/B5010 | 145 °C |
| -- | ISO 306/B120 | 146 °C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 7.0E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.2E-5 cm/cm/°C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Glow Wire Ignition Temperature | 3.0 mm | IEC 60695-2-13 | 875 °C |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 875 °C |
| UL flame retardant rating | 0.40 mm | UL 94 | HB |
| Glow Wire Flammability Index | 0.8 mm | IEC 60695-2-12 | 850 °C |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor? | 100 Hz | ASTM D150 | 1.2E-3 |
| 1 MHz | ASTM D150 | 9.3E-3 | |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms | |
| Volume Resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| Dielectric Strength | 0.800 mm, in Oil | ASTM D149 | 16 KV/mm |
| Dielectric Constant | 100 Hz | ASTM D150 | 2.68 |
| 1 MHz | ASTM D150 | 2.64 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2020 Mpa |
| -- | ISO 527-2/1 | 2150 Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 55.0 Mpa |
| 屈服 | ISO 527-2/50 | 57.0 Mpa | |
| 断裂 3 | ASTM D638 | 50.0 Mpa | |
| 断裂 | ISO 527-2/50 | 60.0 Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 6.0 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| 断裂 3 | ASTM D638 | 98 % | |
| 断裂 | ISO 527-2/50 | 120 % | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2230 Mpa |
| -- 5 | ISO 178 | 2250 Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 85.0 Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 92.0 Mpa |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Screw Speed | 40 到 70 rpm | ||
| Vent Depth | 0.025 到 0.076 mm | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Mold Temperature | 70 到 95 °C | ||
| Processing (Melt) Temp | 295 到 315 °C | ||
| Nozzle Temperature | 290 到 310 °C | ||
| Front Temperature | 295 到 315 °C | ||
| Middle Temperature | 280 到 305 °C | ||
| Rear Temperature | 270 到 295 °C | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 40 到 60 % | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Drying Temperature | 120 °C |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | L 计秤 | ASTM D785 | 89 |
| R 级 | ASTM D785 | 121 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 kJ/m² |
| 23°C | ISO 179/1eA | 70 kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Notched Izod Impact Strength | -30°C | ASTM D256 | 770 J/m |
| 23°C | ASTM D256 | 870 J/m | |
| -30°C 8 | ISO 180/1A | 60 kJ/m² | |
| 23°C 8 | ISO 180/1A | 70 kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 |
| 23°C | ISO 180/1U | 无断裂 | |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 70.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.