PC IUPILON™ GS2010MPH MITSUBISHI ENGINEERING JAPAN
123
Unit Price:$2665 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Filler: Glass fiber reinf 10% filler by weight
- Application Areas:Fiber grade
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | ASTM D955 | 0.3 - 0.5 | % | |
| TD:3.20mm | 0.40to0.60 | % | ||
| MD:3.20mm | 0.30to0.50 | % | ||
| 吸水率 | 饱和,23°C | ISO62 | 0.14 | % |
| 熔体体积流动速率 | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| 熔体质量流动速率 | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| 密度 | ASTM D792/ISO 1183 | 1.26 |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 简支梁无缺口冲击强度 | 23°C | ISO179 | 55 | kJ/m² |
| 拉伸模量 | ASTM D638/ISO 527 | 2900 | kg/cm²(MPa)[Lb/in²] | |
| ISO527-2 | 4500 | Mpa | ||
| 拉伸强度 | 断裂 | ISO527-2 | 78.0 | Mpa |
| 伸长率 | 断裂 | ISO527-2 | 2.9 | % |
| 弯曲模量 | ISO178 | 4000 | Mpa | |
| ASTM D790/ISO 178 | 2700 | kg/cm²(MPa)[Lb/in²] | ||
| 弯曲强度 | ASTM D790/ISO 178 | 90 | kg/cm²(MPa)[Lb/in²] | |
| ISO178 | 135 | Mpa | ||
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | 10 | % |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 线性热膨胀系数 | ASTM D696/ISO 11359 | 5.8.E-05 | mm/mm.℃ | |
| MD | ISO11359-2 | 4E-05 | cm/cm/°C | |
| TD | ISO11359-2 | 6.7E-05 | cm/cm/°C | |
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 145 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 140 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 相比耐漏电起痕指数 | CTI | UL746 | PLC4 |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | V-0 |
| 加工条件 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 模具温度 | 80-120 | °C | ||
| 加工温度 | 270-290 | °C | ||
| 290-310 | °C | |||
| 280-300 | °C | |||
| 干燥条件 | 热风干燥 120℃---約4-8小时 | |||
| 螺杆转速 | 50-100 | rpm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.