PC LEXAN™ EXL9112R SABIC INNOVATIVE US
104
Unit Price:$3952 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility｜Ductility at low temperat｜Short molding cycle
- Application Areas:Electronic and Electrical｜Plastic bag｜lens｜Industrial applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 17 g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 16.0 cm3/10min |
| Modeling Shrinkage | 流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % |
| 横向流动 : 3.20 mm | 内部方法 | 0.40 到 0.80 % | |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.35 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.15 % | |
| Outdoor Suitability | UL 746C | f1 |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 136 °C |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Be | 136 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 123 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10 | ISO 75-2/Ae | 124 °C | |
| Vicat Softening Temperature | -- | ASTM D152511, ISO 306/B5011 | 143 °C |
| -- | ISO 306/B120 | 144 °C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 7.2E-5 cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 130 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| 3.0 mm | UL 94 | 5VA | |
| Glow Wire Flammability Index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 1.0 mm | IEC 60695-2-13 | 825 °C |
| Oxygen Index | ISO 4589-2 | 40 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2260 Mpa |
| -- | ISO 527-2/1 | 2200 Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 58.0 Mpa |
| 屈服 | ISO 527-2/50 | 59.0 Mpa | |
| 断裂 3 | ASTM D638 | 58.0 Mpa | |
| 断裂 | ISO 527-2/50 | 55.0 Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 5.8 % |
| 屈服 | ISO 527-2/50 | 5.0 % | |
| 断裂 3 | ASTM D638 | 100 % | |
| 断裂 | ISO 527-2/50 | 100 % | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2330 Mpa |
| -- 5 | ISO 178 | 2300 Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 88.0 Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 95.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dielectric Strength | 3.20 mm, 在油中 | IEC 60243-1 | 19 KV/mm |
| Relative Permittivity | 50 Hz | IEC 60250 | 2.70 |
| 60 Hz | IEC 60250 | 2.70 | |
| 1 MHz | IEC 60250 | 2.70 | |
| Dissipation Factor? | 50 Hz | IEC 60250 | 4.0E-4 |
| 60 Hz | IEC 60250 | 4.0E-4 | |
| 1 MHz | IEC 60250 | 0.010 | |
| Comparative Tracking Index | IEC 60112 | 175 V |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 120 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 40 到 60 % | ||
| Rear Temperature | 215 到 295 °C | ||
| Middle Temperature | 280 到 305 °C | ||
| Front Temperature | 295 到 315 °C | ||
| Nozzle Temperature | 290 到 310 °C | ||
| Processing (Melt) Temp | 295 到 315 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm | ||
| Vent Depth | 0.025 到 0.076 mm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 95.0 Mpa |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 25 kJ/m² |
| 23°C | ISO 179/1eA | 60 kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 |
| 23°C | ISO 180/1U | 无断裂 | |
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 67.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.