PC LEXAN™ 221R-701 SABIC INNOVATIVE US
113
Unit Price:$2622 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:transparent｜Flame retardant｜enhance
- Application Areas:Household appliances｜Automotive sector
- Color:--
- Grade:--
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific Volume | ASTM D792 | 0.830 cm³/g | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 18 g/10 min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Moisture Absorption | 24 hr | ASTM D570 | 0.15 % |
| 平衡, 23°C | ASTM D570 | 0.35 % | |
| 平衡, 100°C | ASTM D570 | 0.58 % | |
| Outdoor Suitability | UL 746C | f2 |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 129 °C | |
| Vicat Softening Temperature | ASTM D15255 | 154 °C | |
| Coefficient of Linear Thermal Expansion (Flow) | -40 到 95°C | ASTM E831 | 6.8E-5 cm/cm/°C |
| Specific Heat | ASTM C351 | 1250 J/kg/°C | |
| Thermal Conductivity | ASTM C177 | 0.25 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Index of Refraction | ASTM D542 | 1.586 | |
| Transmittance | 2540 µm | ASTM D1003 | 88.0 % |
| Haze | 2540 µm | ASTM D1003 | 1.0 % |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.1 mm | UL 94 | V-2 |
| 6.0 mm | UL 94 | V-0 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Strength | 屈服 | ASTM D638 | 62.0 Mpa |
| 断裂 | ASTM D638 | 68.0 Mpa | |
| Tensile Elongation | 屈服 | ASTM D638 | 7.0 % |
| 断裂 | ASTM D638 | 130 % | |
| Flexural Modulus | 50.0 mm 跨距 | ASTM D790 | 2340 Mpa |
| Flexural Strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 96.0 Mpa |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | > 1.0E+17 ohms·cm | |
| Dielectric Strength | 3.20 mm, in Air | ASTM D149 | 15 KV/mm |
| Dielectric Constant | 60 Hz | ASTM D150 | 3.17 |
| 50 kHz | ASTM D150 | 3.17 | |
| 1 MHz | ASTM D150 | 2.96 | |
| Dissipation Factor? | 50 Hz | ASTM D150 | 9.0E-4 |
| 60 Hz | ASTM D150 | 9.0E-4 | |
| 1 MHz | ASTM D150 | 0.010 | |
| Comparative Tracking Index | UL 746 | PLC 2 | |
| High Amp Arc Ignition | UL 746 | PLC 1 | |
| High Voltage Arc Tracking Rate | UL 746 | PLC 2 | |
| Hot-wire Ignition | UL 746 | PLC 2 |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 120 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 40 到 60 % | ||
| Rear Temperature | 260 到 280 °C | ||
| Middle Temperature | 270 到 295 °C | ||
| Front Temperature | 280 到 305 °C | ||
| Nozzle Temperature | 275 到 300 °C | ||
| Processing (Melt) Temp | 280 到 305 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm | ||
| Vent Depth | 0.025 到 0.076 mm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | M 级 | ASTM D785 | 70 |
| R 级 | ASTM D785 | 118 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 3200 J/m |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 62.0 J |
| Gardner Impact | 23°C | ASTM D3029 | 169 J |
| Tensile Impact Strength | ASTM D1822 | 546 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App