PC IUPILON™ GS2010MR2 MITSUBISHI ENGINEERING JAPAN
146
Unit Price:$3478 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant enhance Filler: Glass fiber reinf 10% filler by weight
- Application Areas:fibre
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Shrinkage rate | TD:3.20mm | 0.40to0.60 | % | |
| MD:3.20mm | 0.30to0.50 | % | ||
| Water absorption rate | Saturation,23°C | ISO62 | 0.14 | % |
| density | ASTM D792/ISO 1183 | 1.27 | ||
| Shrinkage rate | ASTM D955 | 0.3 - 0.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation at break | ASTM D638/ISO 527 | 3.8 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 4400 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 3900 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 130 | kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO527-2 | 4500 | Mpa | |
| tensile strength | Break | ISO527-2 | 78.0 | Mpa |
| elongation | Break | ISO527-2 | 2.9 | % |
| Bending modulus | ISO178 | 4000 | Mpa | |
| bending strength | ISO178 | 135 | Mpa | |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 55 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 145 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 140 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 4E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6.7E-05 | cm/cm/°C | |
| ASTM D696/ISO 11359 | 4.0E-05 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | V-0 |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dry conditions | 热风干燥 120℃---約4-8小时 | |||
| Processing temperature | 270-290 | °C | ||
| 290-310 | °C | |||
| 280-300 | °C | |||
| Screw speed | 50-100 | rpm | ||
| Mold temperature | 80-120 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.