PC LEXAN™ HF1140-111 SABIC INNOVATIVE NANSHA
99
Unit Price:$2941 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 11MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:High mobility Good demolding performanc Good forming performance
- Application Areas:chip container Thin walled products Safety equipment Optical data storage lens
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 特定体积 | ASTM D792 | 0.830 | cm³/g | |
| 熔体质量流动速率 | 300°C/1.2 kg | ASTM D1238 | 25 | g/10 min |
| 熔体体积流动速率 | 300°C/1.2 kg | ISO 1133 | 23.0 | cm3/10min |
| 收缩率 - 流动 | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| 吸水率 | 24 hr | ASTM D570 | 0.15 | % |
| 平衡, 23°C | ASTM D570 | 0.35 | % | |
| 平衡, 100°C | ASTM D570 | 0.58 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 洛氏硬度 | M 级 | ASTM D785 | 70 | |
| R 级 | ASTM D785 | 118 | ||
| 拉伸模量 | -- 2 | ASTM D638 | 2370 | Mpa |
| -- | ISO 527-2/1 | 2350 | Mpa | |
| 拉伸强度 | 屈服 3 | ASTM D638 | 62.0 | Mpa |
| 屈服 | ISO 527-2/50 | 63.0 | Mpa | |
| 断裂 3 | ASTM D638 | 65.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 50.0 | Mpa | |
| 伸长率 | 屈服 3 | ASTM D638 | 6.0 | % |
| 屈服 | ISO 527-2/50 | 6.0 | % | |
| 断裂 3 | ASTM D638 | 120 | % | |
| 断裂 | ISO 527-2/50 | 70 | % | |
| 弯曲模量 | 50.0 mm 跨距 4 | ASTM D790 | 2300 | Mpa |
| -- 5 | ISO 178 | 2300 | Mpa | |
| 弯曲强度 | -- 5, 6 | ISO 178 | 90.0 | Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 93.0 | Mpa | |
| 泰伯耐磨性 | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 | mg |
| 简支梁缺口冲击强度 | -30°C | ISO 179/1eA | 10 | kJ/m² |
| 23°C | ISO 179/1eA | 12 | kJ/m² | |
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 3200 | J/m |
| 装有测量仪表的落镖冲击 | 23°C, Energy at Peak | ASTM D3763 | 54.0 | J |
| 落锤冲击 | 23°C | ASTM D3029 | 169 | J |
| 拉伸冲击强度 | ASTM D1822 | 378 | kJ/m² |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 | °C |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Be | 133 | °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 126 | °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 126 | °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Ae | 121 | °C | |
| 维卡软化点 | -- | ISO 306/B50 | 139 | °C |
| -- | ISO 306/B120 | 140 | °C | |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 | |
| 线形热膨胀系数 - 流动 | -40 到 95°C | ASTM E831 | 6.8E-5 | cm/cm/°C |
| 23 到 80°C | ISO 11359-2 | 7.0E-5 | cm/cm/°C | |
| 比热 | ASTM C351 | 1250 | J/kg/°C | |
| 导热系数 | -- | ASTM C177 | 0.19 | W/m/K |
| -- | ISO 8302 | 0.20 | W/m/K | |
| RTI Elec | UL 746 | 130 | °C | |
| RTI Imp | UL 746 | 130 | °C | |
| RTI | UL 746 | 130 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 表面电阻率 | IEC 60093 | > 1.0E+15 | ohms | |
| 体积电阻率 | -- | ASTM D257 | > 1.0E+17 | ohms·cm |
| -- | IEC 60093 | > 1.0E+15 | ohms·cm | |
| 介电强度 | 3.20 mm, in Air | ASTM D149 | 15 | KV/mm |
| 3.20 mm, 在油中 | IEC 60243-1 | 17 | KV/mm | |
| 介电常数 | 60 Hz | ASTM D150 | 3.17 | |
| 50 kHz | ASTM D150 | 3.17 | ||
| 1 MHz | ASTM D150 | 2.96 | ||
| 50 Hz | IEC 60250 | 2.70 | ||
| 60 Hz | IEC 60250 | 2.70 | ||
| 1 MHz | IEC 60250 | 2.70 | ||
| 耗散因数 | 50 Hz | ASTM D150 | 9.0E-4 | |
| 60 Hz | ASTM D150 | 9.0E-4 | ||
| 1 MHz | ASTM D150, IEC 60250 | 0.010 | ||
| 50 Hz | IEC 60250 | 1.0E-3 | ||
| 60 Hz | IEC 60250 | 1.0E-3 | ||
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 2 | ||
| 高电弧燃烧指数(HAI) | UL 746 | PLC 1 | ||
| 高电压电弧起痕速率 (HVTR) | UL 746 | PLC 2 | ||
| 热丝引燃 (HWI) | UL 746 | PLC 2 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 120 | °C | ||
| 干燥时间 | 3.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 建议注射量 | 40 到 60 | % | ||
| 料筒后部温度 | 250 到 270 | °C | ||
| 料筒中部温度 | 260 到 280 | °C | ||
| 料筒前部温度 | 270 到 295 | °C | ||
| 射嘴温度 | 265 到 290 | °C | ||
| 加工（熔体）温度 | 270 到 295 | °C | ||
| 模具温度 | 70 到 95 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 40 到 70 | rpm | ||
| 排气孔深度 | 0.025 到 0.076 | mm |
| 光学性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 折射率 | ASTM D542 | 1.586 | ||
| 透光率 | 2540 µm | ASTM D1003 | 88.0 | % |
| 雾度 | 2540 µm | ASTM D1003 | 1.0 | % |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 1.1 mm | UL 94 | V-2 | |
| 极限氧指数 | ISO 4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.