PC LEXAN™ 1000 SABIC INNOVATIVE US
109
Unit Price:$2970 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility｜High temperature resistan
- Application Areas:Shell｜Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density / Specific Gravity | ASTMD792 | 1.20 g/cm³ | |
| ISO1183 | 1.20 g/cm³ | ||
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 10 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.50 cm3/10min |
| Modeling Shrinkage | MD：--2 | 内部方法 | 0.50to0.70 % |
| MD：3.20mm | 内部方法 | 0.50to0.70 % | |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| 平衡,23°C | ASTMD570 | 0.35 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 138 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 138 °C | |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 127 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 127 °C | |
| Vicat Softening Temperature | ASTMD152510 | 143 °C | |
| ISO306/B50 | 143 °C | ||
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass |
| Linear thermal expansion coefficient | MD：-40到95°C | ASTME831 | 7E-05 cm/cm/°C |
| MD：23到80°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| Thermal Conductivity | ASTMC177 | 0.20 W/m/K | |
| ISO8302 | 0.20 W/m/K |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Haze | 2540µm | ASTMD1003 | <0.80 % |
| Index of Refraction | ASTMD542 | 1.586 | |
| ISO489 | 1.586 | ||
| Transmittance | 2540µm | ASTMD1003 | 88.0to90.0 % |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 1.6mm | UL94 | V-2 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ASTMD638 | 2350 Mpa | |
| ISO527-2/1 | 2350 Mpa | ||
| Tensile Strength | 屈服 | ASTMD638 | 63.0 Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 63.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 6.0 % |
| Tensile Strain | 屈服 | ISO527-2/50 | 6.0 % |
| Tensile Elongation | 断裂 | ASTMD638 | >70 % |
| Tensile Strain | 断裂 | ISO527-2/50 | >70 % |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 2300 Mpa |
| ISO178 | 2300 Mpa | ||
| Flexural Strength | ISO178 | 90.0 Mpa | |
| Yield,50.0mmSpan | ASTMD790 | 90.0 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume Resistivity | ASTMD257 | >1.0E+15 ohms·cm | |
| IEC60093 | >1.0E+15 ohms·cm | ||
| Dielectric Strength | 1.60mm | ASTMD149 | 27 KV/mm |
| Electric strength | 1.60mm | IEC60243-1 | 27 KV/mm |
| Dielectric Constant | 60Hz | ASTMD150 | 3.00 |
| 1MHz | ASTMD150 | 3.00 | |
| Relative Permittivity | 60Hz | IEC60250 | 3.00 |
| 1MHz | IEC60250 | 3.00 | |
| Dissipation Factor? | 60Hz | ASTMD150 | 1E-03 |
| 1MHz | ASTMD150 | 0.010 | |
| 60Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 0.010 |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 120 |
| R级 | ISO2039-2 | 120 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 65.0 J |
| Notched Izod Impact Strength | 23°C | ASTMD256 | 800 J/m |
| -30°C | ISO180/1A | 12 kJ/m² | |
| 23°C | ISO180/1A | 70 kJ/m² | |
| 23°C | ASTMD4812 | NoBreak | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| 23°C | ISO180/1U | NoBreak |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.