PC LEXAN™ HF1140 SABIC INNOVATIVE US
134
Unit Price:$2831 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility｜Good demolding performanc｜Good forming performance
- Application Areas:chip｜container｜Thin walled products｜Safety equipment｜Optical data storage｜lens
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific Volume | ASTM D792 | 0.830 cm³/g | |
| Melt Mass-Flow Rate | 300°C/1.2 kg | ASTM D1238 | 25 g/10 min |
| Melt Volume flow Rate | 300°C/1.2 kg | ISO 1133 | 23.0 cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Moisture Absorption | 24 hr | ASTM D570 | 0.15 % |
| 平衡, 23°C | ASTM D570 | 0.35 % | |
| 平衡, 100°C | ASTM D570 | 0.58 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 °C |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Be | 133 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 126 °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 126 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 11 | ISO 75-2/Ae | 121 °C | |
| Vicat Softening Temperature | -- | ISO 306/B50 | 139 °C |
| -- | ISO 306/B120 | 140 °C | |
| Ball PressureTest | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Coefficient of Linear Thermal Expansion (Flow) | -40 到 95°C | ASTM E831 | 6.8E-5 cm/cm/°C |
| 23 到 80°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| Specific Heat | ASTM C351 | 1250 J/kg/°C | |
| Thermal Conductivity | -- | ASTM C177 | 0.19 W/m/K |
| -- | ISO 8302 | 0.20 W/m/K | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Index of Refraction | ASTM D542 | 1.586 | |
| Transmittance | 2540 µm | ASTM D1003 | 88.0 % |
| Haze | 2540 µm | ASTM D1003 | 1.0 % |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.1 mm | UL 94 | V-2 |
| Oxygen Index | ISO 4589-2 | 25 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2370 Mpa |
| -- | ISO 527-2/1 | 2350 Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 62.0 Mpa |
| 屈服 | ISO 527-2/50 | 63.0 Mpa | |
| 断裂 3 | ASTM D638 | 65.0 Mpa | |
| 断裂 | ISO 527-2/50 | 50.0 Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 6.0 % |
| 屈服 | ISO 527-2/50 | 6.0 % | |
| 断裂 3 | ASTM D638 | 120 % | |
| 断裂 | ISO 527-2/50 | 70 % | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2300 Mpa |
| -- 5 | ISO 178 | 2300 Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 90.0 Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 93.0 Mpa | |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume Resistivity | -- | ASTM D257 | > 1.0E+17 ohms·cm |
| -- | IEC 60093 | > 1.0E+15 ohms·cm | |
| Dielectric Strength | 3.20 mm, in Air | ASTM D149 | 15 KV/mm |
| 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm | |
| Dielectric Constant | 60 Hz | ASTM D150 | 3.17 |
| 50 kHz | ASTM D150 | 3.17 | |
| 1 MHz | ASTM D150 | 2.96 | |
| 50 Hz | IEC 60250 | 2.70 | |
| 60 Hz | IEC 60250 | 2.70 | |
| 1 MHz | IEC 60250 | 2.70 | |
| Dissipation Factor? | 50 Hz | ASTM D150 | 9.0E-4 |
| 60 Hz | ASTM D150 | 9.0E-4 | |
| 1 MHz | ASTM D150, IEC 60250 | 0.010 | |
| 50 Hz | IEC 60250 | 1.0E-3 | |
| 60 Hz | IEC 60250 | 1.0E-3 | |
| Comparative Tracking Index | UL 746 | PLC 2 | |
| High Amp Arc Ignition | UL 746 | PLC 1 | |
| High Voltage Arc Tracking Rate | UL 746 | PLC 2 | |
| Hot-wire Ignition | UL 746 | PLC 2 |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 120 °C | ||
| Drying Time | 3.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Suggested Shot Size | 40 到 60 % | ||
| Rear Temperature | 250 到 270 °C | ||
| Middle Temperature | 260 到 280 °C | ||
| Front Temperature | 270 到 295 °C | ||
| Nozzle Temperature | 265 到 290 °C | ||
| Processing (Melt) Temp | 270 到 295 °C | ||
| Mold Temperature | 70 到 95 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 40 到 70 rpm | ||
| Vent Depth | 0.025 到 0.076 mm |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | M 级 | ASTM D785 | 70 |
| R 级 | ASTM D785 | 118 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 kJ/m² |
| 23°C | ISO 179/1eA | 12 kJ/m² | |
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 3200 J/m |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 54.0 J |
| Gardner Impact | 23°C | ASTM D3029 | 169 J |
| Tensile Impact Strength | ASTM D1822 | 378 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App