PC Makrolon® 8025 COVESTRO GERMANY
155
Unit Price:$3429 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Filler: Glass fiber with 20% filler by weight
- Application Areas:Fiber grade
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | 23°C | ISO1183 | 1.34 | g/cm³ |
| Apparent density | ISO60 | 0.69 | g/cm³ | |
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 6.5 | g/10min |
| Melt Volume-Flow Rate (MVR) | 300°C/1.2kg | ISO1133 | 6.00 | cm3/10min |
| Shrinkage rate | TD | ISO2577 | 0.30to0.45 | % |
| MD | ISO2577 | 0.30to0.45 | % | |
| TD:2.00mm3 | ISO294-4 | 0.35 | % | |
| MD:2.00mm3 | ISO294-4 | 0.55 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.24 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2/1 | 4000 | Mpa |
| tensile strength | Yield,23°C | ISO527-2/50 | 58.0 | Mpa |
| Break,23°C | ISO527-2/5 | 50.0 | Mpa | |
| Impact strength of simply supported beam without notch | -30°C,Complete Break | ISO179/1eU | 65 | kJ/m² |
| 23°C,Complete Break | ISO179/1eU | 55 | kJ/m² | |
| NotchedIzodImpactStrength | 23°C,CompleteBreak | ISO7391 | 12 | kJ/m² |
| Multi axis Instrumented Impact Energy | -30°C | ISO6603-2 | 10.0 | J |
| 23°C | ISO6603-2 | 20.0 | J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO6603-2 | 2800 | N |
| 23°C | ISO6603-2 | 3300 | N | |
| Ball pressure hardness | ISO2039-1 | 136 | Mpa | |
| elongation | Yield,23°C | ISO527-2/50 | 3.5 | % |
| Break,23°C | ISO527-2/5 | 6.5 | % | |
| TensileCreepModule | 1hr | ISO899-1 | 3700 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 3500 | Mpa |
| Bending modulus | 23°C | ISO178 | 3700 | Mpa |
| bending strength | 3.5%Strain,23°C | ISO178 | 95.0 | Mpa |
| 23°C | ISO178 | 100 | Mpa | |
| Bending strain | 23°C | ISO178 | 5.4 | % |
| CharpyNotchedImpactStrength | 23°C,CompleteBreak | ISO7391 | 12 | kJ/m² |
| Impact strength of simply supported beam without notch | -60°C,CompleteBreak | ISO179/1eU | 65 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ISO306/B50 | 146 | °C |
| -- | ISO306/B120 | 147 | °C | |
| Ball Pressure Test | 137°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 4.5E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 5.5E-05 | cm/cm/°C | |
| Thermal conductivity coefficient | 23°C | ISO8302 | 0.23 | W/m/K |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTI Imp | 1.5mm | UL746 | 115 | °C |
| RTIStr | 1.5mm | UL746 | 125 | °C |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 141 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 134 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 36 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 3.30 | |
| 23°C,1MHz | IEC60250 | 3.30 | ||
| Dissipation factor | 23°C,100Hz | IEC60250 | 1E-03 | |
| 23°C,1MHz | IEC60250 | 9E-03 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 175 | V |
| SolutionB | IEC60112 | 125 | V | |
| Surface resistivity | IEC60093 | 1E+16 | ohms |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | V-2 | |
| 6.0mm | UL94 | V-1 | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 800 | °C |
| 1.5mm | IEC60695-2-12 | 960 | °C | |
| 2.0mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| 4.0mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 0.75mm | IEC60695-2-13 | 850 | °C |
| 2.0mm | IEC60695-2-13 | 875 | °C | |
| 3.0mm | IEC60695-2-13 | 875 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 32 | % | |
| ApplicationofFlamefromSmallBurner MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 | |
| Burning rate - US-FMVSS | >1.00mm | ISO3795 | passed | |
| FlashIgnitionTemperature | ASTMD1929 | 470 | °C | |
| Needle flame test | MethodF:1.50mm | IEC60695-11-5 | 2.0 | min |
| MethodF:2.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodF:3.00mm | IEC60695-11-5 | 2.0 | min | |
| MethodK:1.50mm | IEC60695-11-5 | 1.0 | min | |
| MethodK:2.00mm | IEC60695-11-5 | 1.0 | min | |
| MethodK:3.00mm | IEC60695-11-5 | 2.0 | min | |
| SelfIgnition | ASTMD1929 | 550 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
| ISO Shortcut |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.