PC PANLITE® LD-1000RM TEIJIN JAPAN
163
Unit Price:$3268 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Thermal stability
- Application Areas:Fitness equipment Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 密度 | ASTM D792/ISO 1183 | 1280 | ||
| 收缩率 | ASTM D955 | 0.4-0.6 | % | |
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 0.20 | % | |
| 透光率 | 3mm thick | ASTM D-1003 | white | % |
| 收缩率 | TD:4.00mm | 内部方法 | 0.40到0.60 | % |
| MD:4.00mm | 内部方法 | 0.40到0.60 | % | |
| 吸水率 | 23°C,24hr | ISO62 | 0.20 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | ISO527-2/1 | 2600 | Mpa | |
| 拉伸强度 | 屈服 | ISO527-2/50 | 60.0 | Mpa |
| 断裂 | ISO527-2/50 | 60.0 | Mpa | |
| 伸长率 | 屈服 | ISO527-2/50 | 6.0 | % |
| 断裂 | ISO527-2/50 | 110 | % | |
| 弯曲模量 | ISO178 | 2400 | Mpa | |
| 弯曲应力 | ISO178 | 95.0 | Mpa | |
| 简支梁无缺口冲击强度 | ISO179 | 无断裂 | ||
| 弯曲模量 | ASTM D-790 | 2450(25000) | Mpa(kgf/cm2) | |
| 拉伸率 | 断裂点 | ASTM D-638 | 110 | % |
| 拉伸强度 | 屈服点 | ASTM D-638 | 63(640) | Mpa(kgf/cm2) |
| 断裂点 | ASTM D-638 | 65(660) | Mpa(kgf/cm2) | |
| 弯曲强度 | ASTM D-790 | 95(950) | Mpa(kgf/cm2) | |
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 780(80) | J/m(kgf·cm/cm) |
| 收缩率 | 流动方向 | ASTM D-955 | 0.4～0.6 | % |
| 垂直方向 | ASTM D-955 | 0.4～0.6 | % | |
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 110(11) | J/m(kgf·cm/cm) |
| 断裂伸长率 | ASTM D638/ISO 527 | 110 | % | |
| 拉伸模量 | ASTM D638/ISO 527 | 2500 | kg/cm²(MPa)[Lb/in²] | |
| 弯曲模量 | ASTM D790/ISO 178 | 2300 | kg/cm²(MPa)[Lb/in²] | |
| 弯曲强度 | ASTM D790/ISO 178 | 91 | kg/cm²(MPa)[Lb/in²] |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | ASTM D648/ISO 75 | 125 | ℃（℉） | |
| 维卡软化点 | ASTM D1525/ISO R306 | 139 | ℃（℉） | |
| 线性热膨胀系数 | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ | |
| TD | ISO11359-2 | 7E-05 | cm/cm/°C | |
| RTIElec | 1.5mm | UL746 | 125 | °C |
| RTI Imp | 1.5mm | UL746 | 115 | °C |
| RTI | 1.5mm | UL746 | 125 | °C |
| 线性热膨胀系数 | 流动方向 | ASTM D-696 | 7 | 10-5cm/cm/℃ |
| 垂直方向 | ASTM D-696 | 7 | 10-5cm/cm/℃ | |
| 温度指数 | 电学式，厚度1.47mm | UL 746B | 125 | °C |
| 冲击式，厚度1.47mm | UL 746B | 115 | °C | |
| 非冲击式，厚度1.47mm | UL 746B | 125 | °C | |
| 负荷挠曲温度 | 负荷1.813MPa(18.6kgf/cm2) | JIS K-7207 | 135 | °C |
| 维卡软化点 | ISO306/B50 | 139 | °C | |
| 线性热膨胀系数 | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 137 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 128 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 表面电阻率 | IEC60093 | >1.0E+15 | ohms | |
| 体积电阻率 | IEC60093 | >1.0E+15 | ohms·cm | |
| 介电强度 | IEC60243-1 | 32 | KV/mm | |
| 相对电容率 | 100Hz | IEC60250 | 3.40 | |
| 1MHz | IEC60250 | 3.40 | ||
| 耗散因数 | 100Hz | IEC60250 | 1.1E-03 | |
| 1MHz | IEC60250 | 9E-03 | ||
| 漏电起痕指数 | IEC60112 | 250 | V |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL阻燃等级 | 0.44mm | UL94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.