PC PANLITE® LV-2225Z TEIJIN JAPAN
137
Unit Price:$4544 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:Low viscosity｜transparent｜UV resistance
- Application Areas:Electrical field｜Electronic field｜currency
- Color:--
- Grade:High liquidity level
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 15.0 cm3/10min |
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 % |
| MD:4.00mm | 内部方法 | 0.50to0.70 % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.20 % |
| Modeling Shrinkage | MD2.0mm | ISO294-4 | 0.60 % |
| TD2.0mm | ISO294-4 | 0.60 % | |
| Moisture Absorption | (23°C,24hr) | ISO62 | 0.20 % |
| Melt Mass-Flow Rate | 300℃/1.2Kg | ISO1133 | 11.0 cm3/10min |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 141 °C |
| 1.8MPa,未退火 | ISO75-2/A | 125 °C | |
| Vicat Softening Temperature | ISO306/B50 | 146 °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 cm/cm/°C |
| TD | ISO11359-2 | 7E-05 cm/cm/°C | |
| RTIElec | 1.5mm | UL746 | 125 °C |
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 °C |
| RTIStr | 1.5mm | UL746 | 125 °C |
| Vicat Softening Temperature | ISO306/B50 | 148 °C | |
| Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 7E-05 cm/cm/°C |
| TD | ISO11359-2 | 7E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa未退火 | ISO75-2/Bf | 141 °C |
| 1.80MPa退火 | ISO75-2/Af | 128 °C | |
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 148 ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.7 mm/mm.℃ |
| Optical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Index of Refraction | ASTMD542 | 1.585 | |
| Transmittance | 3000µm | ASTMD1003 | 88.0 % |
| Index of Refraction | ISO489 | 1.59 °C | |
| Light Transmittance (3000μm) | ISO13468-2 | 88.0 % | |
| Transmittance | ASTM D1003/ISO 13468 | 88 % | |
| Index of Refraction | ASTM D542/ISO 489 | 1.585 |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flame Rating | 0.40mm | UL94 | V-2 |
| 1.5mm | UL94 | V-2 | |
| 3.0mm | UL94 | V-2 | |
| Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 850 °C |
| 3.0mm | IEC60695-2-12 | 960 °C | |
| Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 850 °C |
| 3.0mm | IEC60695-2-13 | 875 °C | |
| Fire rating | UL-94 | 0.40mm V-2 | |
| UL-94 | 0.75mm V-2 | ||
| UL-94 | 1.5mm V-2 | ||
| UL-94 | 3.0mm V-2 | ||
| UL-94 | 6.0mm V-2 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Nominal Tensile Strain at Break | ISO527-2/50 | >50 % | |
| Flexural Modulus | ISO178 | 2400 Mpa | |
| Flexural Stress | ISO178 | 94.0 Mpa | |
| Tensile Modulus | ISO527-2/1 | 2400 Mpa | |
| Tensile Stress | 屈服 | ISO527-2/50 | 61.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 6.0 % |
| Tensile Strength | 23°C | ISO527-2 | 61 Mpa |
| Tensile Elongation?(Break) | 23°C | ISO527-2 | 50 % |
| Tensile Modulus | 23°C | ISO527-2 | 2400 Mpa |
| Flexural Strength | 23°C | ISO178 | 94 Mpa |
| Flexural Modulus | 23°C | ISO178 | 2400 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 71 kJ/m² |
| Tensile Modulus | ASTM D638/ISO 527 | /2400 kg/cm²(MPa)[Lb/in²] | |
| Tensile Strength | ASTM D638/ISO 527 | /61 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D638/ISO 527 | /6 % | |
| Flexural Modulus | ASTM D790/ISO 178 | /2400 kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | /94 kg/cm²(MPa)[Lb/in²] |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Dielectric Strength | IEC60243-1 | 30 KV/mm | |
| Dielectric Constant | 100Hz | IEC60250 | 3.10 |
| 1MHz | IEC60250 | 3.00 | |
| Dissipation Factor? | 100Hz | IEC60250 | 1E-03 |
| 1MHz | IEC60250 | 9E-03 | |
| Comparative Tracking Index | IEC60112 | 225 V | |
| Volume Resistivity | IEC60093 | 1E+15 Ω.cm | |
| Surface resistance | IEC60093 | 1E+15 Ω.cm | |
| Insulation strength | IEC60243-1 | 30 KV/mm | |
| Dielectric Constant | 23°C | IEC60250 | 3.00 1MHz |
| Dissipation Factor? | 23°C | IEC60250 | 1E-03 100HZ |
| 23°C | IEC60250 | 9E-03 1MHz | |
| 相对漏电起痕指数 | IEC60112 | 225 V | |
| Dielectric Constant | ASTM D150/IEC 60250 | 3.1 | |
| ASTM D150/IEC 60250 | 3 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak |
| Physical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density | ASTM D792/ISO 1183 | /1200 | |
| Modeling Shrinkage | ASTM D955 | 0.5-0.7 % | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 0.2 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.