POM Delrin® 100PE NC DUPONT NETHERLANDS
146
Unit Price:$6193 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low VOC volatilization thermal stability High temperature resistan UV resistance Hydrolysis resistance wear resistant Chemical resistance High sliding High gloss High rigidity Weather resistance High toughness
- Application Areas:Engine parts Fitness equipment Electronic and electrical Industrial machinery Wear resistant accessorie building materials instrument agriculture Automotive sector Cam
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.42 | g/cm³ | |
| Melt mass flow rate | ISO1133 | 2.6 | g/10min | |
| Melt Volume-Flow Rate (MVR) | 190°C/2.16kg | ISO1133 | 2.20 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.9 | % |
| MD | ISO294-4 | 2.2 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 1.4 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.30 | % | |
| MediumDensity | 1.19 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 3000 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.22 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 2950 | Mpa | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 400 | kJ/m² |
| 23°C | ISO179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 12 | kJ/m² |
| 23°C | ISO180/1A | 14 | kJ/m² | |
| Rockwell hardness | M-Sale | ISO2039-2 | 88 | |
| R-Sale | ISO2039-2 | 119 | ||
| tensile strength | Yield | ISO527-2 | 71.0 | Mpa |
| elongation | Yield | ISO527-2 | 25 | % |
| Nominal tensile fracture strain | ISO527-2 | 45 | % | |
| TensileCreepModule | 1hr | ISO899-1 | 2700 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1500 | Mpa |
| Bending modulus | ISO178 | 2850 | Mpa | |
| bending strength | 3.5%Strain | ISO178 | 77.0 | Mpa |
| Poisson's ratio | ISO527 | 0.35 | ||
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 14 | kJ/m² |
| 23°C | ISO179/1eA | 15 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 155 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 95.0 | °C | |
| vicat softening point | -- | ISO306/A50 | 175 | °C |
| -- | ISO306/B50 | 160 | °C | |
| Melting temperature | ISO11357-3 | 178 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：AnnealingTemperature | ISO11359-2 | 160 | °C | |
| TD：AnnealingTime-Optional | ISO11359-2 | 30.0 | min/mm |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 2E+13 | ohms | |
| Volume resistivity | IEC60093 | 1E+14 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 41 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.90 | ||
| Dissipation factor | 100Hz | IEC60250 | 3.5E-03 | |
| 1MHz | IEC60250 | 5.5E-03 | ||
| Leakage Trace Index | IEC60112 | 600 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00mm | ISO3795 | 50 | mm/min |
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-F-value | refraction | ISO6452 | 91 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg | |
| EmissionofOrganicCompounds | VDA277 | 4.70 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.