POM Delrin® 100AL NC010 DUPONT USA
179
Unit Price:$10862 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity High hardness Thermal stability high viscosity heat-resisting
- Application Areas:Thin walled products Fitness equipment
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.40 | g/cm³ | |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 2.5 | g/10min |
| Shrinkage rate | TD | ISO294-4 | 1.8 | % |
| MD | ISO294-4 | 2.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 3000 | Mpa | |
| tensile strength | Yield | ISO527-2 | 70.0 | Mpa |
| elongation | Yield | ISO527-2 | 18 | % |
| Nominal tensile fracture strain | ISO527-2 | 45 | % | |
| TensileCreepModule | 1hr | ISO899-1 | 2700 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 1500 | Mpa |
| Bending modulus | ISO178 | 2800 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| 23°C | ISO179/1eA | 9.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 170 | kJ/m² |
| 23°C | ISO179/1eU | 250 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 8.0 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 163 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 97.0 | °C | |
| Melting temperature | ISO11357-3 | 178 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| AnnealingTemperature | 160 | °C | ||
| AnnealingTime-Optional | 30.0 | min/mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00mm | ISO3795 | 26 | mm/min |
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS flammability | FMVSS302 | B | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.