POM LNP™ LUBRICOMP™ KL-4540 BK SABIC INNOVATIVE US
145
Unit Price:$3597 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low extract｜Internal lubrication
- Application Areas:Medical and nursing suppl｜Electrical appliances｜Plastic bag
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Modeling Shrinkage | 流动 : 24小时 | ASTM D955 | 2.1 到 2.9 % |
| 横向流动 : 24小时 | ASTM D955 | 2.1 到 2.9 % | |
| Moisture Absorption | 24 hr, 50% RH | ASTM D570 | 0.18 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.43 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 87.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 6 | ISO 75-2/Af | 79.0 °C | |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831 | 1.1E-4 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 1.1E-4 cm/cm/°C |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 1 | ASTM D638 | 1830 Mpa |
| -- | ISO 527-2/1 | 2020 Mpa | |
| Tensile Strength | 屈服 2 | ASTM D638 | 43.0 Mpa |
| 屈服 | ISO 527-2/5 | 39.0 Mpa | |
| 断裂 2 | ASTM D638 | 43.0 Mpa | |
| 断裂 | ISO 527-2/5 | 39.0 Mpa | |
| Tensile Elongation | 屈服 2 | ASTM D638 | 14 % |
| 屈服 | ISO 527-2/5 | 22 % | |
| 断裂 2 | ASTM D638 | 30 % | |
| 断裂 | ISO 527-2/5 | 43 % | |
| Flexural Modulus | 50.0 mm 跨距 3 | ASTM D790 | 2020 Mpa |
| -- 4 | ISO 178 | 2080 Mpa | |
| Flexural Stress | -- | ISO 178 | 60.0 Mpa |
| 断裂, 50.0 mm 跨距 3 | ASTM D790 | 63.0 Mpa | |
| Coefficient of Friction | Dynamic | ASTM D3702 | 0.25 |
| Static | ASTM D3702 | 0.14 | |
| Specific Wear Rate | ASTM D3702 | 1.8E+6 10^-8 mm³/N·m |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 80 °C | ||
| Drying Time | 4.0 hr | ||
| Rear Temperature | 175 到 190 °C | ||
| Middle Temperature | 195 到 205 °C | ||
| Front Temperature | 210 到 220 °C | ||
| Processing (Melt) Temp | 200 到 215 °C | ||
| Mold Temperature | 80 到 110 °C | ||
| Back Pressure | 0.200 到 0.300 Mpa | ||
| Screw Speed | 30 到 60 rpm |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 620 J/m |
| 23°C 6 | ISO 180/1U | 42 kJ/m² | |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 3.00 J |
| -- | ISO 6603-2 | 1.00 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.