POM

POM Delrin® 988P DUPONT USA

242

Unit Price:US$ 2,761 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
140MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜wear resistant
Application Areas:Fitness equipment｜Automotive components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	浸渍Equilibrium点	ASTM D-570	0.90 %
	Water absorption rate	50%相对湿度	ASTM D-570	0.22 %
	Water absorption rate	Water absorption rate	24hr浸渍	ASTM D-570	0.25 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	122℃	ASTM D-638	26 Mpa
Izod Notched Impact Strength	23℃	ASTM D-256	71 J/m
Bending modulus	-55℃	ASTM D-790	4730 Mpa
tensile strength	23℃	ASTM D-638	69 Mpa
Shear strength	23℃	ASTM D-732	66 Mpa
Bending deformation	23℃	ASTM D-790	97 Mpa
Hardness (Rockwell R)		ASTM D-785	120
Elongation at Break	23℃	ASTM D-638	25 %
Bending modulus	70℃	ASTM D-790	1720 Mpa
Elongation at Break	-55℃	ASTM D-638	10 %
Elongation at Break	Elongation at Break	122℃	ASTM D-638	>260 %
Izod Notched Impact Strength	Notched-40℃	ASTM D-256	55 J/m
Compressive stress	23℃，10%变形	ASTM D-695	121 Mpa
tensile strength	70℃	ASTM D-638	48 Mpa
Bending modulus	23℃	ASTM D-638	3640 Mpa
tensile strength	100℃	ASTM D-638	36 Mpa
Bending modulus	100℃	ASTM D-790	1030 Mpa
Elongation at Break	100℃	ASTM D-638	>260 %
Bending modulus	23℃	ASTM D-790	3220 Mpa
Hardness (Rockwell M)		ASTM D-785	94
Flexural fatigue endurance limit	50%RH，23℃，106周期	ASTM D-671	32 Mpa
Bending modulus	122℃	ASTM D-790	755 Mpa
Elongation at Break	70℃	ASTM D-638	180 %
tensile strength	-55℃	ASTM D-638	101 Mpa
Impact strength of cantilever beam gap	23℃	ASTM D-1822	250 kJ/m²
Compressive stress	23℃，1%变形	ASTM D-695	35 Mpa
Hot deformation temperature	140kg/cm2,50℃	ASTM D-621	0.5 %
Izod Notched Impact Strength	Unnotched23℃	ASTM D-256	1620 J/m

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa	ASTM D-648	136
Melting temperature		ASTM D-2133	175
Linear coefficient of thermal expansion	60-104℃	ASTM D-696	13.7 10-5m/m
	Linear coefficient of thermal expansion	104-160℃	ASTM D-696	14.9 10-5m/m
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	29-60℃	ASTM D-696	12.2 10-5m/m
Spontaneous combustion		UL 94	HB
thermal conductivity			0.37 w/mk
Linear coefficient of thermal expansion	-40-29	ASTM D-696	10.4 10-5m/m

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate			1.8-2.0 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity	23℃，0.2%含水量	ASTM D-257	≥14.9 ohm-cm
Arc resistance	3.1mm	ASTM D-495	220 sec
Dielectric strength	2.3mm	ASTM D-149	19.7 KV/mm
Dielectric constant	50%RH，23℃，106Hz	ASTM D-150	0.005
Dielectric constant	Dielectric constant	50%RH，23℃，102-106Hz	ASTM D-150	3.7 ohm-cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

POM Delrin® 988P DUPONT USA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet