POM HOSTAFORM® C9021SW CELANESE USA
140
Unit Price:$4889 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 61.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant currency
- Application Areas:Household appliances Household appliances Automotive sector Fitness equipment Thin walled products
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.8 | % | |
| Water absorption rate | 23℃and50%RH | ISO 62 | 0.2 | % |
| Saturation23℃ | ISO 62 | 0.75 | % | |
| Melt mass flow rate | 8.5cm | ISO 1133 | 12.07 | g/10min |
| ASTM D1238/ISO 1133 | 6.5 | g/10min | ||
| density | ISO 1183 | 1.42 | g/cm | |
| ASTM D792/ISO 1183 | 1420 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 低温-30℃ | ISO 179 1eU | 12 | J/cm |
| 23℃ | ISO 179 1eU | 12.0 | J/cm | |
| ball indentation hardness | 30sec数值 | ISO 2039 part 1 | 140 | Mpa |
| Yield tensile strength | 50mm/min | ISO 527 part 1/2 | 65 | Mpa |
| Tensile creep modulus | 1 hour | ISO 899 part 1 | 2400 | Mpa |
| 1000 hours | ISO 899 part 1 | 1200 | Mpa | |
| Charpy notch impact strength | 23℃ | ISO 179 1eA | 0.6 | J/cm |
| 低温-30℃ | ISO 179 1eA | 0.6 | J/cm | |
| elongation at break | 50mm/min | ISO 527 part 1/2 | 20 | % |
| Tensile modulus | 1mm/min | ISO 527 part 1/2 | 2800 | Mpa |
| elongation | 伸长率 | ISO 527 part 1/2 | 9.0 | % |
| Bending modulus | ISO 178 | 2700 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| melting point | DSC,10 K/min | ISO 3146 method C1b | 166 | °C |
| vicat softening point | VST/B/50 | ISO 306 | 150 | °C |
| Linear coefficient of thermal expansion | 23-55℃ Longitudinal | ISO 11359 part 1/2 | 110 | µm/m-℃ |
| Hot deformation temperature | 1.8MPa | ISO 75 part 1/2 | 100 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | 1 MHz | IEC 60250 | 4.20 | |
| 低频100 Hz | IEC 60250 | 4.20 | ||
| Dissipation factor | IEC 60250 | 0.008 | 1 MHz | |
| 低频100 Hz | IEC 60250 | 0.0025 | ||
| Insulation strength | IEC 60243 part 1 | 35 | KV/mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.