POM KEPITAL® FG2015 KEP KOREA
236
Unit Price:$3674 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity Moderate heat resistance High rigidity Creep resistance
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.5 | ||
| Shrinkage rate | ASTM D955 | 0.8 | % | |
| Melt mass flow rate | ASTM D1238/ISO 1133 | 11.5 | g/10min | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.2 | % | |
| density | ASTM D792 | g/cm³ | ||
| Melt mass flow rate | 190℃/2.16kg | ASTM D1238 | ||
| Shrinkage rate | flow,2.00MM | ASTM D955 | 0.80 | % |
| Water absorption rate | Equilibrium,23℃,60%rh | ASTM D570 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | Yield,23℃ | ASTM D638 | Mpa | |
| tensile elongation | Break,23℃ | ASTM D638 | 3.0 | % |
| Bending modulus | 23°C | ASTM D790 | Mpa | |
| bending strength | 23°C | ASTM D790 | Mpa | |
| Impact strength of cantilever beam gap | 3.20mm | ASTM D256 | J/m | |
| elongation at break | ASTM D638/ISO 527 | 3.6 | % | |
| tensile strength | ASTM D638/ISO 527 | 120 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 5200 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 175 | kg/cm²(MPa)[Lb/in²] | |
| Charpy impact strength | ASTM D256/ISO 179 | 7.0 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal distortion temperature | 1.8MPa,Unannealed | ASTM D648 | °C | |
| Melting temperature | ASTM D3418 | °C | ||
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 164 | ℃（℉） | |
| melting point | 165 | ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 5 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257/IEC 60093 | 1x10的16次方 | Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 1x10的14次方 | Ω.cm | |
| Surface resistivity | ASTM D257 | ohms | ||
| Volume resistivity | ASTM D257 | ohm·cm |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dry conditions | 80-100C（175-210F),3-4hrs | |||
| Processing temperature | 170 | °C | ||
| 200 | °C | |||
| 190 | °C | |||
| 180-210 | °C | |||
| Screw speed | 80~120转/分钟 | rpm | ||
| Mold temperature | 60~80 | °C | ||
| pressure | 注射压力的50%~100% | Mpa | ||
| 5~10kg/cm | Mpa | |||
| 500~1200kg/cm2（7.110~17.070psi） | Mpa |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardant grade | 0.8mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.