PA66 LUMID® GN-2251BF LG CHEM KOREA
136
Unit Price:$3559 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant enhanced grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 吸水率 | 24 hr, 23°C | ASTM D570 | 0.70 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸强度 | 断裂, 23°C, 3.20 mm, 注塑 | ASTM D638 | 123 | Mpa |
| 伸长率 | 断裂, 23°C, 3.20 mm, 注塑 | ASTM D638 | 3.0 | % |
| 洛氏硬度 | R 级, 23°C, 注塑 | ASTM D785 | 125 | |
| 弯曲模量 | 23°C, 3.20 mm, 注塑 | ASTM D790 | 8340 | Mpa |
| 弯曲强度 | 23°C, 3.20 mm, 注塑 | ASTM D790 | 196 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔融峰值温度 | ASTM D3418 | 260 | °C | |
| 线形热膨胀系数 - 流动 | ASTM D696 | 3.0E-5 | cm/cm/°C | |
| RTI | 0.8 mm | UL 746 | 65.0 | °C |
| 1.5 mm | UL 746 | 65.0 | °C | |
| 3.0 mm | UL 746 | 65.0 | °C | |
| RTI Imp | 0.8 mm | UL 746 | 65.0 | °C |
| 1.5 mm | UL 746 | 65.0 | °C | |
| 3.0 mm | UL 746 | 65.0 | °C | |
| RTI Elec | 0.8 mm | UL 746 | 65.0 | °C |
| 1.5 mm | UL 746 | 65.0 | °C | |
| 3.0 mm | UL 746 | 65.0 | °C | |
| 热变形温度 | 1.8 MPa, 未退火, 6.40 mm, 注塑 | ASTM D648 | 225 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 漏电起痕指数 | 解决方案 A | IEC 60112 | 600 | V |
| 介电强度 | 23°C, 1.00 mm | ASTM D149 | 22 | KV/mm |
| 介电常数 | 23°C, 1 MHz | ASTM D150 | 3.00 | |
| 体积电阻率 | 23°C | ASTM D257 | 1.0E+14 | ohms·cm |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 80 到 100 | °C | ||
| 建议的最大水分含量 | 0.10 | % | ||
| 加工（熔体）温度 | 270 到 290 | °C | ||
| 模具温度 | 80 到 110 | °C | ||
| 干燥时间 | 4.0 到 5.0 | hr | ||
| 料筒后部温度 | 265 到 275 | °C | ||
| 料筒中部温度 | 270 到 280 | °C | ||
| 料筒前部温度 | 270 到 285 | °C | ||
| 射嘴温度 | 270 到 280 | °C | ||
| 背压 | 0.981 到 2.94 | Mpa | ||
| 螺杆转速 | 60 到 150 | rpm |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 0.8 mm | UL 94 | V-0 | |
| 1.5 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.