PA66 TORZEN® G3300 L INVISTA USA
128
Unit Price:$3174 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 33% filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glass fiber content | ISO3451/4 | 33 | % | |
| Shrinkage rate | 正常: 2.00 mm | ISO 294-4 | 0.90 到 1.10 | % |
| 平行: 2.00 mm | ISO 294-4 | 0.30到 0.40 | % | |
| Water absorption rate | 23℃, 24 hr | ISO 62 | 1.2 | % |
| Equilibrium, 23℃, 50% RH | ISO 62 | 1.8 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 1.8 | % | |
| Shrinkage rate | TD:2.00mm | ISO294-4 | 0.90到1.1 | % |
| MD:2.00mm | ISO294-4 | 0.30到0.40 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 1.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 10500 | Mpa | |
| tensile strength | Break | ISO527-2 | 205 | Mpa |
| elongation | Break | ISO527-2 | 3.1 | % |
| Bending modulus | ISO178 | 9500 | Mpa | |
| bending strength | ISO178 | 285 | Mpa | |
| Tensile modulus | ISO 527 | 10500 | Mpa | |
| Tensile fracture strength | ISO 527 | 205 | Mpa | |
| Fracture elongation rate | ISO 527 | 3.1 | % | |
| Bending modulus | ISO 178 | 9500 | Mpa | |
| bending strength | ISO 178 | 285 | Mpa | |
| Impact strength of simply supported beam gap | -40℃ | ISO 179 | 10 | kJ/m² |
| 23℃ | ISO 179 | 12 | kJ/m² | |
| Impact strength of cantilever beam gap | 23℃ | ISO 180 | 12 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75 | 255 | °C |
| 1.82 MPa, Unannealed | ISO 75 | 248 | °C | |
| Melting temperature | 10℃/min | ISO 11357 | 262 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 248 | °C |
| Melting temperature | ISO11357-3 | 262 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 255 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.